Enhanced TDS
Identification & Functionality
- Blend
- No
- CI Name
- CI Number
- Chemical Family
- Pigment Type
- Product Code
- MITM12557
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
Properties
- Physical Form
- Notes
- * - Minor elements may arise from the raw materials used. However, these are firmly bound to the crystal lattice as ions.
- ** - Binder test paste is based on white cement
Packaging & Availability
- Packaging Type
Other
- Apparent Tamped Density
- 0.8-1.2 g/mL
- Appearance
- Black pigment powder
- Appearance (SDS)
- Powder
- Bulk Density (SDS)
- 300.0-1000.0 kg/m³
- Color (SDS)
- Black
- Color Difference
- max. 1.5
- Color Intensity
- 95.0-105.0 %
- Color Scale
- -0.8-0.8 CIELAB
- Color Scale
- -0.8-0.8 CIELAB
- Decomposition Temperature (SDS)
- min. 176.0 °F
- Density
- 4.6 g/mL
- Density (SDS)
- 4.6 g/cm³
- Group Principal Number
- S000008
- Insoluble in (SDS)
- Water
- Iron Concentration
- 86.0-95.0 %
- Iron Concentration
- 86.0-95.0 %
- Item Number
- Loss on Ignition
- max. 5.0 %
- Melting Point (SDS)
- min. 1832.0 °F
- Moisture Content
- max. 4.0 %
- Odor (SDS)
- Odorless
- Oil Absorption
- 21.0 g/100g
- Particle Size
- 0.15 µm
- Principal
- pH (SDS)
- 4.0-8.0
- Optical Properties
Value Units Test Method / Conditions Color Difference max. 1.5 - Delta E, Reduction with Titanium dioxide (1:5) Color Intensity 95.0-105.0 % % Color Scale -0.8-0.8 CIELAB CIELAB Delta a, Titanium dioxide reduction, 1:5 Color Scale -0.8-0.8 CIELAB CIELAB Delta B, titanium dioxide reduction, 1:5 - Chemical Properties
Value Units Test Method / Conditions Loss on Ignition max. 5.0 % % DIN 55913 at 1000°C, 0.5h - Physical Properties
Value Units Test Method / Conditions Apparent Tamped Density 0.8-1.2 g/mL g/mL DIN EN ISO 787-11 Density 4.6 g/mL g/mL DIN EN ISO 787-10 Moisture Content max. 4.0 % % DIN EN ISO 787-2 Oil Absorption 21.0 g/100g g/100g DIN EN ISO 787-5 Particle Size 0.15 µm µm Scanning Electron Microscopy (SEM) - Material Composition
Value Units Test Method / Conditions Iron Concentration 86.0-95.0 % % As Ferric Oxide Iron Concentration 86.0-95.0 % % α - Iron(III) Oxide Content - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Bulk Density (SDS) 300.0-1000.0 kg/m³ kg/m³ Decomposition Temperature (SDS) min. 176.0 °F °F Density (SDS) 4.6 g/cm³ g/cm³ at 20°C Melting Point (SDS) min. 1832.0 °F °F pH (SDS) 4.0-8.0 - 5% Concentration