Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Function
- Pour Point Depressant, Resin
- Industrial Additives Functions
- Plastics & Elastomers Functions
- Product Code
- MITM01633
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Labeling Claims
- Materials Features
- Key Features
- The high Vinyl Acetate content of EVATANE® 20-20 brings softness, flexibility and polarity. EVATANE® 20-20 is compatible with most tackifying resins and waxs.
- Combined with a high fluidity, it is an efficient and easy handling product for hot melt adhesives formulations. It can also be used as an additive for crude oil (pour point depressant), bitumen modification and cables compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Industrial Additives End Use
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
Properties
- Physical Form
- Soluble In
Technical Details & Test Data
- Processing Parameters
- EVATANE® 20-20 can be processed on most conventional equipment used for thermoplastics.
- It is recommended to avoid melt temperatures above 230°C and to purge the equipment after a run is completed.
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage Conditions
- EVATANE® 20-20 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- White
- Decomposition Temperature (SDS)
- 500.0 °F
- Density
- 0.94 g/cm³
- Density (SDS)
- 0.95 g/cm³
- Elongation at Break
- 600.0 %
- Elongation at Break
- 600.0 %
- Group Principal Number
- S002377
- Hardness
- 89.0 HV
- Hardness
- 89.0 Shore A
- Hardness
- 89.0 HV
- Insoluble in (SDS)
- Water
- Item Number
- Melt Flow Index
- 20.0 g/10min
- Melt Flow Index
- 20.0 g/10min
- Melting Point
- 83.0 °C
- Melting Point (SDS)
- 181.0 °F
- Odor (SDS)
- Ester like
- Principal
- Shelf Life
- 3.0 yr
- Softening Point
- 127.0 °C, 127.0 °C
- Softening Point
- 46.0 °C
- Softening Point
- 127.0 °C
- Softening Point
- 46.0 °C
- Softening Point
- 127.0 °C
- Tensile Strength at Break
- 17.0 MPa
- Tensile Strength at Break
- 17.0 MPa
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break1 600.0 % % ASTM D638 Elongation at Break2 600.0 % % ISO 527 Hardness3 89.0 HV HV ASTM D2240 Hardness4 89.0 Shore A Shore A Shore Durometer Scale Hardness5 89.0 HV HV ISO 868 Tensile Strength at Break6 17.0 MPa MPa ASTM D638 Tensile Strength at Break 17.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Melt Flow Index 20.0 g/10min g/10min ASTM D1238 at 190°C, 2.16 kg Melt Flow Index 20.0 g/10min g/10min ISO 1133 at 190°C , 2.16 kg Melting Point 83.0 °C °C ISO 11357-3 Softening Point 127.0 °C °C Ring and Ball Test Softening Point 127.0 °C °C Ring and Ball Test Softening Point 46.0 °C °C ASTM D1525 10N,on compression molded samples Softening Point 127.0 °C °C ASTM E28 Softening Point 46.0 °C °C ISO 306 10N Softening Point 127.0 °C °C NF EN 1238 - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) 500.0 °F °F Density (SDS) 0.95 g/cm³ g/cm³ Melting Point (SDS) 181.0 °F °F