Enhanced TDS
Identification & Functionality
- Chemical Family
- Industrial Additives Functions
- Product Code
- MITM16524
- Technologies
- Product Families
Applications & Uses
- Industrial Additives End Use
- Markets
- Applications
- Processing Information
OREVAC® 18343 is suitable for the production of cable compounds with most common types of equipment (internal mixer, co-kneader, twin screw extruder). Typical extrusion temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Exit Fittings- Channels Die 180 - 190°C 190 - 200°C 200 - 210°C 210 - 220°C 220 - 230°C 220 - 240°C 220 - 240°C
Properties
- Physical Form
Storage & Handling
- Storage Information
OREVAC® 18343 should be stored in dry conditions, protected from UV-light. Improper storage conditions may cause degradation and have consequences on physical properties of the product. Three years from the date of delivery, in unopened packaging.
Other
- ADR/RID/ADN Proper Shipping Name
- Not Applicable
- ADR/RID/ADN UN Number
- Not Applicable
- Appearance (SDS)
- Pellets
- Color (SDS)
- White natural color
- Decomposition Temperature (SDS)
- min. 280.0 °C
- Density
- 0.92 g/cm³
- Density (SDS)
- 918.0 kg/m³
- Elongation at Break
- min. 700.0 %
- Elongation at Break
- min. 700.0 %
- Group Principal Number
- S002377
- IATA/ICAO Proper Shipping Name
- Not Applicable
- IATA/ICAO UN Number
- Not Applicable
- IMO/IMDG Proper Shipping Name
- Not Applicable
- IMO/IMDG UN Number
- Not Applicable
- Insoluble in (SDS)
- Water
- Item Number
- Melt Flow Index
- max. 2.0 g/10min
- Melting Point
- 121.0 °C
- Melting Point (SDS)
- 121.0 °C
- Odor (SDS)
- No odor
- Other Hazards
- Contact with hot material - prevent serious burns. May be irritating to the respiratory system. The product is not biodegradable.
- Principal
- Softening Point
- 97.0 °C
- Softening Point
- 97.0 °C
- Softening Point
- 97.0 °C
- Softening Point (SDS)
- 95.0 °C
- Solubility In Water (SDS)
- max. 1.0 mg/L
- Tensile Modulus
- 210.0 MPa
- Tensile Modulus
- 210.0 MPa
- Tensile Strength at Break
- min. 18.0 MPa
- Tensile Strength at Break
- min. 18.0 MPa
- Mechanical Properties
Value Units Test Method / Conditions Elongation at Break min. 700.0 % % ASTM D638 on compression molded samples Elongation at Break min. 700.0 % % ISO 527-2 on compression molded samples Tensile Modulus 210.0 MPa MPa ASTM D638 on compression molded samples Tensile Modulus 210.0 MPa MPa ISO 527-2 on compression molded samples Tensile Strength at Break min. 18.0 MPa MPa ASTM D638 compression molded Tensile Strength at Break min. 18.0 MPa MPa ISO 527-2 on compression molded samples - Physical Properties
Value Units Test Method / Conditions Density 0.92 g/cm³ g/cm³ ISO 1183 Melt Flow Index max. 2.0 g/10min g/10min ISO 1133 at 190°C , 2.16 kg Melting Point 121.0 °C °C ISO 11357-3 Softening Point 97.0 °C °C ASTM D1525 at 10N Softening Point 97.0 °C °C ISO 306 at 10N Softening Point 97.0 °C °C Vicat Softening Point Test at 10N - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 280.0 °C °C Density (SDS) 918.0 kg/m³ kg/m³ Melting Point (SDS) 121.0 °C °C Softening Point (SDS) 95.0 °C °C Solubility In Water (SDS) max. 1.0 mg/L mg/L