Bayoxide® E 8710

Principal: Lanxess IPG

Pigment Type: Inorganic Pigments

Color (Properties): Black

Chemical Family: Iron Oxides

CI Name: Pigment Black 11

CI Number: 77489

View All Documents

Enhanced TDS

Identification & Functionality

Blend
No
CI Name
CI Number
Chemical Family
Chemical Name
Pigment Type
Product Code
MITM07279
Single Ingredient
Yes
Synonyms
Diiron trioxide, Ferric oxide
Technologies
Product Families

Properties

Color (Properties)
Physical Form
Note
  • 35 The magnetic data were measured with a magnetometer MA7 at a maximum field strength of 5 kOe assuming a density of 4.6 g/cm3
  • 53 Minor elements may arise from the raw materials used. However, these are firmly bound to the crystal lattice as ions.

Regulatory & Compliance

Packaging & Availability

Packaging Type
Packaging Information
  • Product is available in sacks and bulky bags.

Storage & Handling

Storage Conditions
  • Protect against weathering. Store in a dry place and avoid extreme fluctuations in temperature.
  • When storing large quantities of pigments, temperatures above 80 °C must be avoided as an alteration (oxidation) of the pigment may be caused by heat.
  • Special conditions for opened packaging: Close bags after use to prevent the absorption of moisture and contamination.

Other

Appearance (SDS)
Powder
Bulk Density (SDS)
300.0-1000.0 kg/m³
Coercivity
90.0-105.0 Oe
Color (SDS)
Black
Density
4.6 g/mL
Ferric Oxide Content
min. 98.0 %
Insoluble in (SDS)
Water
Item Number
Melting Point (SDS)
min. 1832.0 °F
Moisture Content
1.0 %
Odor (SDS)
Odorless
Other Hazards
None known.
Particle Size
0.5 µm
Principal
Remanence
13.0-16.8 emu/g
Saturation Magnetization
84.8-91.7 emu/g
Specific Surface Area
3.0-6.0 m²/g
pH
4.5-7.5
pH (SDS)
4.0-8.0
Chemical Properties
ValueUnitsTest Method / Conditions
pH4.5-7.5-DIN EN ISO 787-9
Physical Properties
ValueUnitsTest Method / Conditions
Coercivity90.0-105.0 OeOeMagnetometer MA7
Density4.6 g/mLg/mLDIN EN ISO 787-10
Moisture Content1.0 %%DIN EN ISO 787-2 ex works
Particle Size0.5 µmµmScanning Electron Microscopy (SEM)
Remanence13.0-16.8 emu/gemu/gMagnetometer MA7
Saturation Magnetization84.8-91.7 emu/gemu/gMagnetometer MA7
Specific Surface Area3.0-6.0 m²/gm²/g
Material Composition
ValueUnitsTest Method / Conditions
Ferric Oxide Contentmin. 98.0 %%
SDS Physical and Chemical Properties
ValueUnitsTest Method / Conditions
Bulk Density (SDS)300.0-1000.0 kg/m³kg/m³
Melting Point (SDS)min. 1832.0 °F°F
pH (SDS)4.0-8.0-at 5%