Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Composite Materials Functions
- Function
- Resins, Binders & Matrix Materials
- Product Code
- MITM16055
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Key Features
- Low viscosity
- Rapid cure
- Excellent toughness
- No post cure required
Applications & Uses
- Additives Information
- Crestapol® 1210 may be filled with a variety of fillers, such as calcium carbonate or alumina trihydrate, with a particle size of less than 5μ.
Properties
- Physical Form
Technical Details & Test Data
- Post Curing
- Without post cure, Crestapol® 1210 reaches approximately 94% of their total cure.
- Therefore, no post cure is required.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S003002
- Principal
Storage & Handling
- Storage Conditions
- Crestapol® 1210 should be stored in the dark in suitable closed containers.
- It is recommended that the storage temperature should be less than 20°C where practical, but should not be above 30°C.
- Ideally, containers should be opened immediately prior to use.
- Where they have to be stored outside, it is recommended that containers be kept in a horizontal position to avoid the possible ingress of water.
Other
- Appearance
- Clear yellowish brown
- Color (SDS)
- Transparent
- IATA/ICAO Proper Shipping Name
- Resin solution
- IATA/ICAO UN Number
- UN1866
- IMO/IMDG EmS Fire
- F-E
- IMO/IMDG EmS Spill
- S-E
- IMO/IMDG Proper Shipping Name
- Resin solution
- IMO/IMDG UN Number
- UN1866
- Item Number
- MEX/NOM Proper Shipping Name
- Resin, solutions
- MEX/NOM UN Number
- UN1866
- Odor (SDS)
- Solvent
- Other Hazards
- None known
- Protect from Freezing
- No
- TDG Canada Proper Shipping Name
- Resin solution
- TDG Canada UN Number
- UN1866
- Temperature Control
- Yes
- USA/DOT Proper Shipping Name
- Resin solution
- USA/DOT UN Number
- UN1866
- Material Composition
Value Units Test Method / Conditions Glass Content 30.0 % % C.S.M (Made with 4 layers 450g/m² PB CSM) Laminate Volatile Content 36.0 % % - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 1.7 % % C.S.M (Made with 4 layers 450g/m² PB CSM) Laminate Elongation at Break 3.3 % % Resin (Without Post-Cure) Flexural Modulus 7.9 GPa GPa C.S.M (Made with 4 layers 450g/m² PB CSM) Laminate Flexural Strength 211.0 MPa MPa C.S.M (Made with 4 layers 450g/m² PB CSM) Laminate Hardness 44.0 HV HV resin without post-cure Tensile Modulus 8.0 GPa GPa C.S.M (Made with 4 layers 450g/m² PB CSM) Laminate Tensile Modulus 3.5 GPa GPa resin without post-cure Tensile Strength 128.0 MPa MPa C.S.M (Made with 4 layers 450g/m² PB CSM) Laminate Tensile Strength 79.0 MPa MPa resin without post-cure - Physical Properties
Value Units Test Method / Conditions Gelling Time 8.5 m m with 2% Accelerator G², 2.0% Accelerator D¹ (Crestapol 1210 only), 1.5% Trigonox 44B at 20°C Gelling Time 3.0 m m with 2% Accelerator G², 2.0% Accelerator D¹ (Crestapol 1210 only), 1.5% Trigonox 44B at 20°C, to peak Peak Temperature 153.0 °C °C with 2% Accelerator G², 2.0% Accelerator D¹ (Crestapol 1210 only), 1.5% Trigonox 44B at 20°C Specific Gravity 1.1 - at 25°C Storage Temperature -100.0-86.0 °F °F Viscosity 1.75 P P At 25°C - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Flash Point (SDS) 28.0 °C °C Closed Cup Kinematic Viscosity (SDS) min. 40.0 mm²/s mm²/s At 40°C Relative Density (SDS) 1.1-1.2 - - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 6.0 mo mo - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature 93.0 °C °C at 1.80MPa, Resin (Without Post-Cure)