Features & Benefits
- Ready-to-Use Product Features
- Product Benefits
- Thermal and mechanical stability
- Superior mechanical stability versus other thickeners, particularly in the presence of heat and water
- High dropping point, typically in excess of 300 °C.
- Load carrying & Wear protection
- Enhanced EP and AW properties
- Does not require the use of additional additives .Resistance to Water
- Excellent resistance to water washout and spray-off. Corrosion Resistance
- Sulfonates are known and used for their excellent rust prevention properties
- This property is inherent in the thickener
- Will easily outperform all other technologies . Resistance to Oxidation
- The use of a premium antioxidant and a high quality oil ensures excellent thermal and oxidation stability
Applications & Uses
- Application Area
- Markets
- Applications
- Product Applications
G-2181-2 Grease is a low viscosity synthetic formulation which offers superior performance over a wide operating temperature range. It is formulated for low temperature operations. It can be used in high speed bearings, sealed for life bearings, and in most extended life operations. It easily exceeds the requirements for NLGI GC/LB certification.
Properties
- Physical Form
Packaging & Availability
- Packaging Information
Petroleum Lubricating Grease available in a wide range of containers.
Storage & Handling
- Handling Information
G-2186-2 Grease may be handled using conventional grease handling and dispensing methods.
Other
- Appearance (SDS)
- Paste
- Bearing Life Performance
- 200.0 hr
- Bomb Oxidation Pressure Drop
- 6.0 psi
- Color (SDS)
- Tan
- Copper Strip Corrosion Test Rating
- 1B
- Density (SDS)
- 0.95-1.05 g/cm³
- Drop Point
- 605.0 °F
- Flash Point (SDS)
- 180.0-200.0 °C
- Grease Leakage Tendency
- 4.0 gm
- Group Principal Number
- S000008
- Insoluble in (SDS)
- Water
- Kinematic Viscosity
- 39.0 cSt
- Load Wear Index
- 65.0 kgf
- Load Wear Index
- 65.0 kgf
- Mechanical Stability Change
- 4.0 %
- Mobility
- 25.8 g/min
- Odor (SDS)
- Weak hydrocarbon like
- Oil Separation
- 0.0 %
- Principal
- Salt Fog Corrosion Resistance
- min. 1000.0 hr
- Scar Diameter
- 0.42 mm
- Scar Diameter
- 0.42 mm
- Timken OK Load Test
- 27.2 kg
- Torque
- 5200.0 g-cm
- Torque
- 1600.0 g-cm
- Vapor Pressure (SDS)
- max. 8.0 hPa
- Water Washout Loss
- 0.5 %
- Weld Point
- 500.0 kg
- Thermal Properties
Value Units Test Method / Conditions Bomb Oxidation Pressure Drop 6.0 psi psi ASTM D942 per 1000 Hours - Shelf Life & Stability
Value Units Test Method / Conditions Salt Fog Corrosion Resistance min. 1000.0 hr hr ASTM B117 Salt Fog - Mechanical Properties
Value Units Test Method / Conditions Bearing Life Performance 200.0 hr hr ASTM D3527 Load Wear Index 65.0 kgf kgf ASTM D2596 Load Wear Index 65.0 kgf kgf Four-Ball Extreme Pressure Test Mechanical Stability Change 4.0 % % ASTM D217 100000 strokes Scar Diameter 0.42 mm mm ASTM D2266 Scar Diameter 0.42 mm mm Four Ball Wear Test Timken OK Load Test 27.2 kg kg ASTM D2509 Torque 5200.0 g-cm g-cm ASTM D1478 at 55°C Torque 1600.0 g-cm g-cm ASTM D1478 at 55°C , 1 hour Weld Point 500.0 kg kg - Physical Properties
Value Units Test Method / Conditions Drop Point 605.0 °F °F ASTM D2265 Grease Leakage Tendency 4.0 gm gm ASTM D4290 Kinematic Viscosity 39.0 cSt cSt ASTM D445 at 40°C, Base Oil Mobility 25.8 g/min g/min US Steel Mobility Test at 350°C Oil Separation 0.0 % % ASTM D1742 Water Washout Loss 0.5 % % ASTM D1264 at 80°C , removed - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Density (SDS) 0.95-1.05 g/cm³ g/cm³ At 77°F Flash Point (SDS) 180.0-200.0 °C °C Vapor Pressure (SDS) max. 8.0 hPa hPa At 77°F