Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM11205
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Key Features
- OREVAC® 18342N has been designed to develop a reliable bonding strength with polyethylene or most ethylene copolymers and many kinds of different materials among which polyamides and EVOH.
- OREVAC® 18342N can be processed by means of different extrusion and coextrusion technologies including blown and cast coextrusion film, blow molding and tube coextrusion.
- OREVAC® 18342N also develops adhesion onto FBE (Fusion Bonded Epoxy) steel pipe protective layer.
Applications & Uses
- Compatible Polymers & Resins
- Plastics & Elastomers Processing Methods
- Markets
- Applications
Properties
- Physical Form
Technical Details & Test Data
- Processing Parameters
OREVAC® 18342N is to be processed like a standard polyethylene resin. Typical extrusion temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Exit Fittings Channels Die 190-200°C 200°C 200-210°C 210-220°C 220-230°C 220-240°C 220-240°C Final profile and settings will depend on the line and the multi-layer structure being run.
Packaging & Availability
Storage & Handling
- Storage Conditions
OREVAC® 18342N should be stored in dry conditions protected from UV-light. Improper storage conditions may cause degradation and have consequences on physical properties of
the product.Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Bulk Density (SDS)
- 500.0 kg/m³
- Color (SDS)
- White
- Decomposition Temperature (SDS)
- min. 280.0 °C
- Density
- 0.93 g/cm³
- Density
- 0.93 g/cm³
- Density (SDS)
- 0.914 g/cm³
- Elongation at Break
- min. 600.0 %
- Elongation at Break
- min. 600.0 %
- Hardness
- 59.0 HV
- Hardness
- 59.0 Shore D
- Hardness
- 59.0 HV
- Item Number
- Melt Flow Index
- 3.5 g/10min
- Melt Flow Index
- 3.5 g/10min
- Melting Point
- 125.0 °C
- Melting Point (SDS)
- 248.0 °F
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation., The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases: Irritating to eyes, respiratory system and skin. Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure)., Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- Principal
- Shelf Life
- 3.0 yr
- Softening Point
- 110.0 °C
- Softening Point
- 110.0 °C
- Solubility In Water (SDS)
- max. 1.0 mg/L
- Tensile Modulus
- 310.0 MPa
- Tensile Modulus
- 310.0 MPa
- Tensile Strength at Break
- min. 20.0 MPa
- Tensile Strength at Break
- min. 20.0 MPa
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break1 min. 600.0 % % ASTM D638 Elongation at Break2 min. 600.0 % % ISO 527 Hardness3 59.0 HV HV ASTM D2240 Hardness4 59.0 Shore D Shore D Shore Durometer Scale Hardness5 59.0 HV HV ISO 868 Tensile Modulus 310.0 MPa MPa ASTM D638 on compression molded samples Tensile Modulus 310.0 MPa MPa ISO 527-2 on compression molded samples Tensile Strength at Break min. 20.0 MPa MPa ASTM D638 Tensile Strength at Break min. 20.0 MPa MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density 0.93 g/cm³ g/cm³ ISO 1183 Density 0.93 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 3.5 g/10min g/10min ASTM D1238 at 190°C, 2.16 kg Melt Flow Index 3.5 g/10min g/10min ISO 1133 at 190°C , 2.16 kg Melting Point 125.0 °C °C ISO 11357-3 Softening Point 110.0 °C °C ASTM D1525 10N Softening Point 110.0 °C °C ISO 306 10N - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Bulk Density (SDS) 500.0 kg/m³ kg/m³ Decomposition Temperature (SDS) min. 280.0 °C °C Density (SDS) 0.914 g/cm³ g/cm³ at 20°C Melting Point (SDS) 248.0 °F °F Solubility In Water (SDS) max. 1.0 mg/L mg/L