Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Function
- Resin
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM13665
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Processing Information
Injection 446°F / 482°F / 536°F
Melt Temperature (Min / Recommended / Max) Mold 20 – 60°C Temperature Drying (only necessary for containers opened for more than two hours) 12 hours/ 176°F/ -40°F
Time/Temperature/Desiccant bed dryer
Properties
- Physical Form
- Soluble In
- Notes
* - Samples conditioned 15 days, 23°C - 50 % R.H.
Packaging & Availability
- Packaging Type
- Product Packaging
Rilsan® BESHV BLACK T is delivered dried in sealed packaging ready to be processed. For best results in gas pipe extrusion, additional desiccant bed drying to maintain/achieve moisture values < 0.02% is recommended.
Other
- Carbon Content
- min. 95.0 %
- Charpy Impact Strength
- 11.0 kJ/m²
- Charpy Impact Strength
- 10.0 kJ/m²
- Color (SDS)
- Black
- Decomposition Temperature (SDS)
- min. 662.0 °F
- Density
- 1.03 g/cm³
- Flexural Modulus
- 171000.0 psi
- Hardness
- 72.0 Shore D
- Hardness
- 77.0 Shore D
- Hardness
- 72.0 Shore A
- Hardness
- 77.0 Shore A
- Insoluble in (SDS)
- Water
- Item Number
- Melting Point
- 372.0 °F
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation., Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- Principal
- Shelf Life
- 2.0 yr
- Strain at Break
- min. 200.0 %
- Strain at Yield
- 5.0 %
- Stress at Break
- 7540.0 psi
- Stress at Yield
- 6090.0 psi
- Tensile Modulus
- 202000.0 psi
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 11.0 kJ/m² kJ/m² ISO 179 at -22°F, V-notched Charpy Impact Strength 10.0 kJ/m² kJ/m² ISO 179 at 73°F, V-notched Flexural Modulus 171000.0 psi psi ISO 178 each 15 days Hardness 72.0 Shore D Shore D at 15 sec Hardness 77.0 Shore D Shore D instantaneous Hardness 72.0 Shore A Shore A ISO 868 after 15 secs Hardness 77.0 Shore A Shore A ISO 868 instantaneous Strain at Break min. 200.0 % % ISO 527 at 15 days, at break Strain at Yield 5.0 % % ISO 527 at yield, 15 days Stress at Break 7540.0 psi psi ISO 527 at 15 days, at break Stress at Yield 6090.0 psi psi ISO 527 at yield, 15 days Tensile Modulus 202000.0 psi psi ISO 527 each 15 days - Physical Properties
Value Units Test Method / Conditions Density 1.03 g/cm³ g/cm³ ISO 1183 Melting Point 372.0 °F °F ISO 11357 - Material Composition
Value Units Test Method / Conditions Carbon Content min. 95.0 % % ASTM D6866 calculated - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 662.0 °F °F