- Anti-Caking Agent, Flow Promoter, Carrier
- Product Code
- MITM04371
- Single Ingredient
- Yes
- Synonyms
- Calcium hydrosilicate, Calcium monosilicate, Calcium polysilicate, Calcium silicate, E 552
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Product Applications
SIPERNAT® 880 can be used as a carrier for acid sensitive active ingredients in plant protection requiring a slightly alkaline pH-value. In addition, SIPERNAT® 880 is an auxiliary in polychloroprene adhesives.
Properties
- Physical Form
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000006
- Principal
Storage & Handling
- Storage Conditions
Our silica products are inert and extremely stable chemically. However, due to their high specific surface area, they can absorb moisture and volatile organic compounds from the surrounding atmosphere. Therefore, we recommend storing the products in sealed containers in a dry, cool place, and removed from volatile organic substances. Even if a product is stored under these conditions, after a longer period it can still pick up ambient moisture over time, which could lead to its exceeding the specified moisture content. For this reason, our recommended use-by date is 24 months after date of manufacture. Product more than 24 months old should be tested for moisture content before use in order to make certain that it is still suitable for the intended application.
Other
- Color (SDS)
- White
- Item Number
- Odor (SDS)
- Odorless
- Other Hazards
- None
- USA/DOT UN Number
- Not Applicable
- Optical Properties
Value Units Test Method / Conditions Brightness min. 95.0 % % DIN 53163 Y - Chemical Properties
Value Units Test Method / Conditions Loss on Ignition max. 10.5 % % ISO 3262-1 At 1000°C, 2 H Loss on Ignition max. 2.0 % % Internal Method at 1000°C, 2h, based on ignited substance pH 10.5 - ISO 787-9 5% in Water - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 24.0 mo mo - Physical Properties
Value Units Test Method / Conditions Apparent Tamped Density 260.0 g/L g/L ISO 787-11 Dioctyl Adipate Absorption 130.0 ml/100 g ml/100 g Internal Method based on original substance Moisture Content max. 7.0 % % ISO 787-2 at 105°C, 2 hours Particle Size 8.5 µm µm ISO 13320 D50 Particle Size 8.5 µm µm Malvern Laser Diffraction Method D50 Sieve Fractionation (Retained) max. 0.15 % % ISO 787 Mocker Specific Surface Area 35.0 m²/g m²/g ISO 9277 Multipoint, nitrogen - Material Composition
Value Units Test Method / Conditions Chloride Content max. 1.0 % % Internal Method based on original substance Iron Content max. 400.0 ppm ppm Internal Method at 1000°C, 2h, based on ignited substance Silicon Content min. 87.0 % % ISO 3262-19 at 1000°C, 2h, based on ignited substance, as silicon dioxide - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 1700.0 °C °C Density (SDS) 2.0 g/cm³ g/cm³ DIN EN ISO 787-10 at 20°C Melting Point (SDS) 1700.0 °C °C pH (SDS) 10.5 - at 20°C, 50 g/l Suspension