BONDINE® TX8030 is a versatile adhesive for extrusion coating or lamination, designed as:
- Concentrate to be used in dry blend with LDPE. BONDINE® TX8030 improves adhesion of LDPE on aluminum foils, metallized or primerized films.
- Ready for use resin to be used pure. LOTADER® TX8030 gives excellent adhesion on substrates likes aluminum foil, metallized plastics, paper, board, PE and its copolymers.
- Coextrusion tie layer for PE/PA in extrusion coating process.
Properties
- Physical Form
- Soluble In
Regulatory & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Processing
Heat stability of acrylate comonomers allows processing temperatures as high as for polyamides, which is the main material using BONDINE® TX8030 as impact modifier. However, to minimize the generation of gels, it is recommended to purge the equipment with LDPE after a run is completed. BONDINE® TX8030 is not corrosive.
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage Conditions
BONDINE® TX8030 is usually packed in waterproof bags or rigid containers with waterproof liner. It should be stored in dry conditions and be kept out of moisture in an aerated building.
Improper storage conditions may cause degradation and could have consequences on physical properties of the product. It is recommended to reseal the bag or the liner after use to
protect BONDINE® TX8030 against moisture.Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- Colorless
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Slightly acrylic
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure), Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 700.0 % ASTM D638 Elongation at Break 700.0 % ISO 527 Flexural Modulus 130.0 MPa ISO 178 Flexural Modulus 130.0 MPa ISO 178 Hardness 36.0 HV ASTM D2240 Hardness 36.0 Shore D Shore Durometer Scale Hardness 36.0 HV ISI 868 on compression molded samples Tensile Strength at Break 12.0 MPa ASTM D638 Tensile Strength at Break 12.0 MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ ISO 1183 Density 0.94 g/cm³ ASTM D1505 Melt Flow Index 3.0 g/10min ISO 1133 at 190°C, 2.16kg Melting Point 95.0 °C ISO 11357-3 Softening Point 65.0 °C ASTM D1525 10N Softening Point 65.0 °C ISO 306 10N - Material Composition
Value Units Test Method / Conditions Ethyl Acrylate Content 13.0 %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) Maleic Anhydride Content 2.8 %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 842.0 °F Bulk Density (SDS) approx. 500.0 kg/m³ Decomposition Temperature (SDS) min. 572.0 °F Density (SDS) 0.94 g/cm³ at 20°C