Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM15433
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Adhesive & Sealant End Applications
- Compatible Polymers & Resins
- Plastics & Elastomers Processing Methods
- Processing Information
LOTADER® 9304T can be processed on most conventional equipment used for thermoplastics. It is recommended to avoid overheating above 230°C and to purge the equipment after a run is completed.
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage Conditions
- LOTADER® 9304T should be stored in dry conditions protected from UV-light. Improper storage conditions may cause degradation and have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Contact with hot material - prevent serious burns. May be irritating to the respiratory system. The product is not biodegradable.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 700.0 % % ASTM D638 Elongation at Break 700.0 % % ISO 527 Hardness 82.0 HV HV ASTM D2240 Hardness 82.0 Shore A Shore A Shore Durometer Scale Hardness 82.0 HV HV ISO 868 Tensile Strength at Break 26.0 MPa MPa ASTM D638 Tensile Strength at Break 26.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ISO 1183 Density 0.94 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 75.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 75.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 80.0 °C °C ISO 11357-3 Softening Point 49.0 °C °C ASTM D1525 10N Softening Point 150.0 °C °C ASTM E28 at 10N, on compression molded samples Softening Point 49.0 °C °C ISO 306 Softening Point 150.0 °C °C Ring and Ball Test at 10N, on compression molded samples - Material Composition
Value Units Test Method / Conditions Maleic Anhydride Content 1600.0 ppm ppm Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 662.0 °F °F Decomposition Temperature (SDS) min. 500.0 °F °F Melting Point (SDS) 158.0-230.0 °F °F DIN 51007 Melting Point (SDS) 158.0-230.0 °F °F Melting Point (SDS) 158.0-230.0 °F °F Differential Scanning Calorimetry Melting Point (SDS) 158.0-230.0 °F °F Differential Thermal Analysis Relative Density (SDS) 0.93-0.95 - at 20°C