Enhanced TDS
Identification & Functionality
- Chemical Family
- Chemical Name
- Plastics & Elastomers Functions
- Product Code
- MITM10759
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Processing Information
Heat stability of acrylate comonomer allows processing temperatures as high as for polyesters (PBT, PET) and PPS.
CAUTION:
- LOTADER® AX8930 reacts with polymers containing maleic anhydride and acid. This reaction may generate gels or can block an extruder if not controlled. Extruders must be thoroughly purged before and after extrusion.
Properties
- Physical Form
- Soluble In
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage Conditions
- LOTADER® AX8930 should be stored in dry conditions and be kept out of moisture in an aerated building. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Due to its physical properties (Vicat temperature <40°C), it may be possible that the LOTADER® AX8930 shows some caking. This is particularly true during summer time.
- Three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- Colorless
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Slightly acrylic
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break min. 1000.0 % % ASTM D638 Elongation at Break min. 1000.0 % % ISO 527 Flexural Modulus max. 30.0 MPa MPa ASTM D790 Flexural Modulus max. 30.0 MPa MPa ISO 178 Tensile Strength at Break 4.0 MPa MPa ASTM D638 Tensile Strength at Break 4.0 MPa MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Melt Flow Index 7.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 7.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 65.0 °C °C ISO 11357-3 Softening Point max. 40.0 °C °C ASTM D1525 10N Softening Point max. 40.0 °C °C ISO 306 10N - Material Composition
Value Units Test Method / Conditions Glycidyl Methacrylate Content 3.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) Methyl Acrylate Content 25.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 450.0-842.0 °F °F Bulk Density (SDS) 500.0 kg/m³ kg/m³ Decomposition Temperature (SDS) 300.0-572.0 °F °F Density (SDS) 940.0 kg/m³ kg/m³ at 68°F Melting Point (SDS) 149.0-163.0 °F °F