Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Chemical Name
- Plastics & Elastomers Functions
- Product Code
- MITM01693
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Product Benefits
- Due to the methyl acrylate content, LOTRYL® 20MA08 can be used for applications where softness, flexibility, and polarity are required.
- Typical applications are extrusion coating, co-extrusion, and compounds.
Applications & Uses
- Compatible Substrates & Surfaces
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Product Applications
- Due to the methyl acrylate content, LOTRYL® 18MA02 can be used for applications where softness, flexibility, and polarity are required.
- Typical applications are extrusion coating, coextrusion, and compounds.
Properties
- Physical Form
Technical Details & Test Data
- Processing Details
LOTRYL® 20MA08 can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 20MA08 is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 18MA02 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Two years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Autoignition Temperature (SDS)
- 662.0 °F
- Bulk Density (SDS)
- 500.0 kg/m³
- Color (SDS)
- White
- Decomposition Temperature (SDS)
- min. 662.0 °F
- Density
- 0.94 g/cm³
- Density
- 0.94 g/cm³
- Density
- 0.94 g/cm³
- Density
- 0.94 g/cm³
- Density (SDS)
- 0.92-0.98 g/cm³
- Elongation at Break
- 700.0 %
- Elongation at Break
- 700.0 %
- Flexural Modulus
- 50.0 MPa
- Flexural Modulus
- 50.0 MPa
- Group Principal Number
- S002377
- Hardness
- 25.0 Shore D
- Hardness
- 25.0 Shore D
- Hardness
- 25.0 Shore D
- Insoluble in (SDS)
- Water
- Item Number
- Melt Flow Index
- 2.0-3.0 g/10min
- Melt Flow Index
- 2.0-3.0 g/10min
- Melting Point
- 83.0 °C
- Melting Point (SDS)
- 158.0-221.0 °F
- Methyl Acrylate Content
- 17.0-20.0 %(W/W)
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation., The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin., Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure)., Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- Principal
- Shelf Life
- 2.0 yr
- Softening Point
- 53.0 °C
- Softening Point
- 53.0 °C
- Softening Point
- 53.0 °C
- Tensile Strength at Break
- 13.0 MPa
- Tensile Strength at Break
- 13.0 MPa
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 700.0 % % ASTM D638 Elongation at Break 700.0 % % ISO 527-2 Flexural Modulus1 50.0 MPa MPa ASTM D790 Flexural Modulus2 50.0 MPa MPa ISO 178 Hardness 25.0 Shore D Shore D Hardness 25.0 Shore D Shore D ASTM D2240 Hardness 25.0 Shore D Shore D ISO 868 Tensile Strength at Break3 13.0 MPa MPa ASTM D638 Tensile Strength at Break 13.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ISO 1183 at 23°C Density 0.94 g/cm³ g/cm³ ASTM D1505 at 23°C Density 0.94 g/cm³ g/cm³ ASTM D150 at 23°C Density 0.94 g/cm³ g/cm³ ISO 1193 at 23°C Melt Flow Index 2.0-3.0 g/10min g/10min ASTM D1238 at 190°C, 2.16 kg Melt Flow Index 2.0-3.0 g/10min g/10min ISO 1133 at 190°C , 2.16 kg Melting Point 83.0 °C °C ISO 11357-3 Softening Point 53.0 °C °C ASTM D1525 at 10N Softening Point 53.0 °C °C ISO 306 at 10N Softening Point 53.0 °C °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 17.0-20.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 662.0 °F °F Bulk Density (SDS) 500.0 kg/m³ kg/m³ At 68°F Decomposition Temperature (SDS) min. 662.0 °F °F Density (SDS) 0.92-0.98 g/cm³ g/cm³ at 68°F Melting Point (SDS) 158.0-221.0 °F °F