Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Compatible Substrates & Surfaces
- Plastics & Elastomers Processing Methods
- Product Applications
- Due to the methyl acrylate content, LOTRYL® 20MA08 can be used for applications where softness, flexibility and polarity are required.
- Typical applications are extrusion coating, co-extrusion and compounds.
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Processing Information
- LOTRYL® 20MA08 can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed.
- If LOTRYL® 20MA08 is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Information
- LOTRYL® 20MA08 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 800.0 % % ASTM D638 Elongation at Break 800.0 % % ISO 527-2 Flexural Modulus 20.0 MPa MPa ASTM D790 Flexural Modulus 20.0 MPa MPa ISO 178 Hardness 83.0 Shore A Shore A Hardness 83.0 Shore A Shore A ASTM D2240 Hardness 83.0 Shore A Shore A ISO 868 Tensile Strength at Break 9.0 MPa MPa ASTM D638 Tensile Strength at Break 9.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ASTM D150 at 23°C Density 0.94 g/cm³ g/cm³ ISO 1193 at 23°C Melt Flow Index 8.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 8.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 76.0 °C °C ISO 11357-3 Softening Point 46.0 °C °C ASTM D1525 at 10N Softening Point 46.0 °C °C ISO 306 at 10N Softening Point 46.0 °C °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 20.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 662.0 °F °F Bulk Density (SDS) 500.0 kg/m³ kg/m³ At 68°F Decomposition Temperature (SDS) min. 662.0 °C °C Density (SDS) 0.92-0.98 g/cm³ g/cm³ at 68°F