Enhanced TDS
Identification & Functionality
- Chemical Family
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM13290
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Properties
Packaging & Availability
- Packaging Type
Other
- Appearance (SDS)
- Powder
- Application Temperature
- 240.0 °C
- Application Temperature
- 70.0 °C
- Autoignition Temperature (SDS)
- min. 300.0 °C
- Burning Rate
- 60.0 mm/min
- Burning Rate
- 60.0 mm/min
- Butadiene Content
- 27.0 %
- Color (SDS)
- Colorless to light yellow
- Decomposition Temperature (SDS)
- min. 300.0 °C
- Density
- 1.02 g/cm³
- Elongation at Break
- min. 5.0 %, min. 5.0 %
- Flexural Modulus
- 1720.0 MPa
- Freeze Point (SDS)
- min. 120.0 °C
- Glow-Wire Flammability Index
- 700.0 °C
- Hardness
- 72.0 HV
- Insoluble in (SDS)
- Insoluble in water
- Item Number
- Izod Impact Strength
- 365.0 kg-cm/cm
- Izod Impact Strength
- 270.0 kg-cm/cm
- Izod Impact Strength
- 190.0 kg-cm/cm
- Izod Impact Strength
- 28.0 kg-cm/cm
- Izod Impact Strength
- 21.0 kg-cm/cm
- Melt Flow Index
- 4.0 g/10min
- Melt Volume-Flow Rate
- 14.0 cc/10min
- Monomer Content
- 0.03 %
- Other Hazards
- Dust may cause irritation of the respiratory system. Melted product can cause severe burns.
- Principal
- Relative Density (SDS)
- 1.05
- Softening Point
- 93.0 °C
- Stress at Yield
- 32.0 MPa
- Stress at Yield
- 35.0 MPa
- Stress at Yield
- 35.0 MPa
- Tensile Modulus
- 1600.0 MPa
- Tensile Modulus
- 1600.0 MPa
- USA/DOT Proper Shipping Name
- Not Applicable
- USA/DOT UN Number
- Not Applicable
- Yellowness Index
- 31.0
- Optical Properties
Value Units Test Method / Conditions Yellowness Index 31.0 - ASTM E313 at 23°C - Thermal Properties
Value Units Test Method / Conditions Burning Rate 60.0 mm/min mm/min ISO 3795 250x105x2mm Burning Rate 60.0 mm/min mm/min US-FMVSS 250x105x2mm Glow-Wire Flammability Index 700.0 °C °C IEC 60695-2-12 2.0 mm - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break min. 5.0 % % ISO 527 at 23°C, 50% H.R, 50 mm/min Elongation at Break min. 5.0 % % ISO 527 at 23°C, 50% H.R, 50 mm/min Flexural Modulus 1720.0 MPa MPa ISO 178 at 23°C, 50% H.R, 2 mm/min Hardness 72.0 HV HV at 23°C, 50% H.R, Ball Indentation Izod Impact Strength 365.0 kg-cm/cm kg-cm/cm ASTM D256 at 23°C, 50% H.R, (3.2mm) 1/8”, notched Izod Impact Strength 270.0 kg-cm/cm kg-cm/cm ASTM D256 at 23°C, 50% H.R, (6.4mm) 1/4, notched Izod Impact Strength 190.0 kg-cm/cm kg-cm/cm ASTM D256 at C,-23° 50% H.R, (6.4mm) 1/4”, notched Izod Impact Strength 28.0 kg-cm/cm kg-cm/cm ISO 180-1A at 23°C, 50% humidity ratio, notched Izod Impact Strength 21.0 kg-cm/cm kg-cm/cm ISO 180-1A at -30°C, 50% H.R, notched Stress at Yield 32.0 MPa MPa ASTM D638 at 23°C, 50% H.R, 5 mm/min Stress at Yield 35.0 MPa MPa ISO 527-1 at 23°C, 50% H.R, 5 mm/min Stress at Yield 35.0 MPa MPa ISO 527-2 at 23°C, 50% H.R, 5 mm/min Tensile Modulus 1600.0 MPa MPa ISO 527-1 at 23°C, 50% H.R, 1 mm/min Tensile Modulus 1600.0 MPa MPa ISO 527-2 at 23°C, 50% H.R, 1 mm/min - Physical Properties
Value Units Test Method / Conditions Density 1.02 g/cm³ g/cm³ ISO 1183-1 at 25°C Melt Flow Index 4.0 g/10min g/10min ASTM D1238 at 230°C, 3.8 kg Melt Volume-Flow Rate 14.0 cc/10min cc/10min ISO 1133 at 220°C, 10kg Softening Point 93.0 °C °C ISO 306 B50:50°C/h - Material Composition
Value Units Test Method / Conditions Butadiene Content 27.0 % % Infrared Spectroscopy At 23°C Monomer Content 0.03 % % Gas Chromatography at 23°C, as residual - Application Information
Value Units Test Method / Conditions Application Temperature 240.0 °C °C ISO 294 Application Temperature 70.0 °C °C ISO 294 Injection Molding - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 300.0 °C °C Decomposition Temperature (SDS) min. 300.0 °C °C Freeze Point (SDS) min. 120.0 °C °C Relative Density (SDS) 1.05 - at 20°C