Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM09936
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Key Features
- OREVAC® IM800 has been designed to be used as a high impact modifier for a large range of engineering polymers such as polyamides (PA6, PA66, PA12 etc.).
- Due to its properties (softness, reactivity), OREVAC® IM300/IM300N is especially suitable when high performance at low temperature (-40°C) are required.
Applications & Uses
Properties
- Physical Form
Technical Details & Test Data
- Processing Parameters
OREVAC®IM800 can be processed over a wide range of conditions. Compounding can be achieved on conventional equipment with usual temperatures needed for polyamides
modification.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage Conditions
- OREVAC® IM800 should be stored in dry conditions protected from UV-light. Improper storage conditions may cause degradation and have consequences on physical properties of the product.
- Due to its physical properties (Vicat temperature <40°C), it may be possible that the OREVAC® IM800 shows some caking.
- Three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- Translucent
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- None
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness (severity of effects depends on extent of exposure), Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break min. 800.0 % % ASTM D638 Elongation at Break min. 800.0 % % ISO 527 Flexural Modulus 6.0 MPa MPa ASTM D790 Flexural Modulus 6.0 MPa MPa ISO 178 Hardness 20.0 Shore D Shore D Hardness 70.0 Shore A Shore A Shore Durometer Scale Hardness 70.0 HV HV ISO 868 Tensile Strength at Break min. 6.0 MPa MPa ASTM D638 Tensile Strength at Break min. 6.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.87 g/cm³ g/cm³ ISO 1183 Density 0.87 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 0.8 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 0.8 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 55.0 °C °C ISO 11357-3 Softening Point max. 40.0 °C °C ASTM D1525 10N Softening Point max. 40.0 °C °C ISO 306 10N - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Density (SDS) 0.863 g/cm³ g/cm³ Melting Point (SDS) 117.0 °F °F