Enhanced TDS
Identification & Functionality
- Additives Included
- Blend
- Yes
- Chemical Family
- Polymer Name
- Product Code
- MITM14869
- Single Ingredient
- No
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
Properties
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Technical Data
Viscosity-shear Rate
Shearstress-shear Rate
Stress-strain
Secant Modulus-strain
Stress-strain (Isochronous) 23°C
Creep Modulus - Time 23°C
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000003
- Principal
Other
- Color (SDS)
- Colorless to slightly yellow
- Item Number
- Odor (SDS)
- Odorless
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Thermal Properties
Value Units Test Method / Conditions Coefficient of Thermal Expansion 0.0002 /K /K ISO 11359-1 parallel, dry Specific Heat 2800.0 J/kg.K J/kg.K dry, of melt Thermal Conductivity 0.18 W/m·K W/m·K - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Electrical Properties
Value Units Test Method / Conditions Comparative Tracking Index 600.0 - IEC 60112 condensed Dielectric Constant 6.0 - IEC 60250 at 100 Hz, dry Dielectric Constant 6.0 - IEC 60250 at 1MHz, dry Dielectric Strength 36.0 kV/mm kV/mm IEC 60243-1 dry basis Dissipation Factor 0.0552 tan δ tan δ IEC 60250 100Hz, dry Dissipation Factor 0.0378 tan δ tan δ IEC 60250 1MHz, dry Surface Resistance 3000000000000.0 Ω Ω IEC 60093 condensed Volume Resistivity 13000000000.0 Ω-cm Ω-cm IEC 60093 dry basis - Mechanical Properties
Value Units Test Method / Conditions Compression Set 19.0 % % ISO 815 at 23°C, 24 h, Dry Hardness 22.0 Shore D Shore D Hardness 77.0 Shore A Shore A Shore Durometer Scale Hardness 22.0 Shore A Shore A ISO 868 Strain at Break min. 50.0 % % ISO 527-1 Dry, at break Strain at Break min. 300.0 % % ISO 527-1 dry, thermoplastic elastomer, at break Strain at Break min. 50.0 % % ISO 527-2 at break, condensed Stress 4.0 MPa MPa ISO 527-1 dry, at 100% elongation Stress 1.0 MPa MPa ISO 527-1 dry, at 10% elongation Stress 3.0 MPa MPa ISO 527-1 dry, at 50% strain Stress 3.0 MPa MPa ISO 527-2 condensed, at 50% strain Stress at Break 32.0 MPa MPa ISO 527-1 dry, thermoplastic elastomer, at break Tear Strength 44.0 kN/m kN/m ISO 34-1 dry basis Tensile Modulus 12.0 MPa MPa ISO 527-1 dry basis Tensile Modulus 10.0 MPa MPa ISO 527-2 condensed Volume Loss 130.0 mm³ mm³ ISO 4649 Dry, Abrasion Resistance - Physical Properties
Value Units Test Method / Conditions Density 830.0 kg/m³ kg/m³ dry, liquid Density 1000.0 kg/m³ kg/m³ ISO 1183 condensed Density 1000.0 kg/m³ kg/m³ ISO 1183 dry basis Glass Transition Temperature (Tg) -65.0 °C °C ISO 11357-1 at 10°C/min, dry Humidity Absorption 0.4 % % ISO 62 dry basis Load/Unload Temperature 42.0 °C °C ISO 75-1 at 0.45 MPa, dry, deflection under load Melting Point 134.0 °C °C ISO 11357-1 at 10°C/min Mold Shrinkage 0.8 % % ISO 2577 normal, dry Mold Shrinkage 0.5 % % ISO 2577 parallel, dry Mold Shrinkage 0.8 % % ISO 294-4 normal, dry Mold Shrinkage 0.5 % % ISO 294-4 parallel, dry Softening Point 58.0 °C °C ISO 306 at 50°C/h, 50N, dry Thickness 1.6 mm mm Dry Water Absorption 1.2 % % ISO 62 dry basis - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) 572.0-662.0 °F °F Melting Point (SDS) 273.0 °F °F