Identification & Functionality
- Additives Included
- Blend
- Yes
- Chemical Family
- Polymer Name
- Product Code
- MITM01782
- Single Ingredient
- No
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Processing Information
- Typical melt temperature (Min / Recommended / Max) : 230°C / 260°C / 290°C
- Typical mold temperature : 25 – 60°C
- Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 65-75°C
Properties
Packaging & Availability
- Packaging Type
- Product Packaging
This grade is delivered dried in sealed packaging (20 or 25 kg bags) ready to be processed.
Other
- Autoignition Temperature (SDS)
- 698.0-842.0 °F
- Bulk Density (SDS)
- 550.0-650.0 kg/m³
- Charpy Impact Strength
- 20.0 kJ/m²
- Color (SDS)
- Colorless to slightly yellow
- Decomposition Temperature (SDS)
- 572.0-662.0 °F
- Density
- 1010.0 kg/m³
- Hardness
- 58.0 Shore A
- Heat of Combustion (SDS)
- 34.0-37.0 kJ/kg
- Humidity Absorption
- 0.7 %
- Insoluble in (SDS)
- Water
- Item Number
- Melting Point
- 169.0 °C
- Melting Point (SDS)
- 336.0 °F
- Mold Shrinkage
- 1.4 %
- Mold Shrinkage
- 1.2 %
- Mold Shrinkage
- 1.4 %
- Mold Shrinkage
- 1.2 %
- Net Calorific Value (SDS)
- 34.0-37.0 kJ/kg
- Nominal Strain at Break
- min. 50.0 %
- Nominal Strain at Break
- min. 50.0 %
- Odor (SDS)
- Odorless
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation., Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- Principal
- Shelf Life
- 2.0 yr
- Softening Point
- 157.0 °C
- Strain at Yield
- 22.0 %
- Strain at Yield
- 22.0 %
- Stress at Yield
- 19.0 MPa
- Stress at Yield
- 18.0 MPa
- Tensile Modulus
- 307.0 MPa
- Tensile Modulus
- 285.0 MPa
- Water Absorption
- 1.1 %
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 20.0 kJ/m² kJ/m² ISO 179-1EA at -30°C, condensed, notched Hardness 58.0 Shore A Shore A ISO 868 Nominal Strain at Break min. 50.0 % % ISO 527-1 dry, at break, nominal Nominal Strain at Break min. 50.0 % % ISO 527-2 condensed, at break, nominal Strain at Yield 22.0 % % ISO 527-1 Dry Strain at Yield 22.0 % % ISO 527-2 condensed Stress at Yield 19.0 MPa MPa ISO 527-1 dry, at yield Stress at Yield 18.0 MPa MPa ISO 527-2 condensed, at yield Tensile Modulus 307.0 MPa MPa ISO 527-1 Dry Tensile Modulus 285.0 MPa MPa ISO 527-2 condensed - Physical Properties
Value Units Test Method / Conditions Density 1010.0 kg/m³ kg/m³ ISO 1183 Dry Humidity Absorption 0.7 % % ISO 62 Dry Melting Point 169.0 °C °C ISO 11357-1 at 10°C/min Mold Shrinkage 1.4 % % ISO 2577 normal, dry Mold Shrinkage 1.2 % % ISO 2577 parallel, dry Mold Shrinkage 1.4 % % ISO 294-4 normal, dry Mold Shrinkage 1.2 % % ISO 294-4 parallel, dry Softening Point 157.0 °C °C ISO 306 at 50°C/h, 50N, dry Water Absorption 1.1 % % ISO 62 Dry - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 698.0-842.0 °F °F ASTM D1929 Bulk Density (SDS) 550.0-650.0 kg/m³ kg/m³ Decomposition Temperature (SDS) 572.0-662.0 °F °F Heat of Combustion (SDS) 34.0-37.0 kJ/kg kJ/kg Melting Point (SDS) 336.0 °F °F Net Calorific Value (SDS) 34.0-37.0 kJ/kg kJ/kg NF M 03-005