Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Function
- Resin
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM14914
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Processing Information
Injection Molding, Film Extrusion, Profile Extrusion, Other Extrusion
- Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
- Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 65-80°C.
Properties
- Physical Form
Technical Details & Test Data
- Technical Data
Viscosity-shear Rate
Shearstress-shear Rate
Stress-strain
Secant Modulus-strain
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000003
- Principal
Other
- Color (SDS)
- Translucent
- Item Number
- Odor (SDS)
- Odorless
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Electrical Properties
Value Units Test Method / Conditions Dielectric Strength 30.0 kV/mm kV/mm IEC 60243-1 dry basis - Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 15.0 kJ/m² kJ/m² ISO 179-1EA at 23°C, condensed, notched Charpy Impact Strength 13.0 kJ/m² kJ/m² ISO 179-1EA at -30°C, condensed, notched Hardness 71.0 Shore D Shore D condensed Hardness 71.0 Shore A Shore A ISO 868 condensed Nominal Strain at Break min. 50.0 % % ISO 527-1 condensed, at break, nominal Nominal Strain at Break min. 50.0 % % ISO 527-2 condensed, at break, nominal Strain at Yield 36.0 % % ISO 527-1 condensed Strain at Yield 36.0 % % ISO 527-2 condensed Tensile Modulus 1180.0 MPa MPa ISO 527-1 condensed Tensile Modulus 1180.0 MPa MPa ISO 527-2 condensed Weld Load 10.0 kg kg ISO 1133 at 235°C - Physical Properties
Value Units Test Method / Conditions Density 1030.0 kg/m³ kg/m³ ISO 1183 condensed Density 1030.0 kg/m³ kg/m³ ISO 1183 dry basis Melt Volume-Flow Rate 6.0 cc/10min cc/10min ISO 1133 at 235°C Melting Point 186.0 °C °C ISO 11357-3 at 10°C/min Melting Point 186.0 °C °C ISO 11357-1 at 10°C/min Water Absorption 1.9 % % ISO 62 condensed - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) 350.0 °C °C Density (SDS) 1.0-1.5 g/cm³ g/cm³ Lower Explosion Limit (SDS) 100.0 % % at 85⁰C Melting Point (SDS) 347.0-374.0 °F °F Specific Gravity (SDS) 1.0-1.5 - Water = 1, liquid