Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Country of Origin
- Function
- Resin
- Plastics & Elastomers Functions
- Product Code
- MITM15919
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Processing Information
Injection Molding
- Typical melt temperature (Min / Recommaneded / Max) : 250°C / 280°C / 300°C
- Typical mold temperature : 20 - 80 °C
- Dyring time and temperature (only for bags opened for more than two hours): 4 - 6 hours at 90°C
Properties
- Physical Form
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000003
- Principal
Other
- Color (SDS)
- Translucent, transparent
- Item Number
- Odor (SDS)
- Odorless
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- Temperature Control
- Yes
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Carbon Content 62.0 % ASTM D6866 - Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 6.0 kJ/m² ISO 179-1EA at 23°C, dry, notched Charpy Impact Strength 9.0 kJ/m² ISO 179-1EA at -30°C, dry, notched Hardness 76.0 Shore D at 15 sec Hardness 76.0 Shore A ISO 868 at 15 sec Nominal Strain at Break min. 50.0 % ISO 527-1 condensed, at break, nominal Nominal Strain at Break min. 50.0 % ISO 527-2 condensed, nominal Strain at Yield 66.0 % ISO 527-1 condensed Strain at Yield 66.0 % ISO 527-2 condensed Tensile Modulus 1665.0 MPa ISO 527-1 condensed Tensile Modulus 1665.0 MPa ISO 527-2 condensed - Optical Properties
Value Units Test Method / Conditions Light Transmittance 92.0 % ISO 13468-1 Light Transmittance 92.0 % ISO 13468-2 - Physical Properties
Value Units Test Method / Conditions Density 1000.0 kg/m³ ISO 1183 condensed Density 1000.0 kg/m³ ISO 1183 dry basis Glass Transition Temperature (Tg) 120.0 °C ISO 11357-1 at 10°C/min, dry Glass Transition Temperature (Tg) 120.0 °C ISO 11357 at 10°C/min, dry Humidity Absorption 1.16 % ISO 62 at 23°C, 50% RH, dry, equilibrium Load/Unload Temperature 85.0 °C ISO 75-1 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 73.0 °C ISO 75-1 at 1.80 MPa, dry, deflection under load Load/Unload Temperature 85.0 °C ISO 75-2 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 73.0 °C ISO 75-2 at 1.80 MPa, dry, deflection under load Melt Volume-Flow Rate 8.0 cm³/10 min ISO 1133 at 275°C, 2.16 kg, dry Mold Shrinkage 0.7 % ISO 2577 normal, dry Mold Shrinkage 0.6 % ISO 2577 parallel, dry Mold Shrinkage 0.7 % ISO 294-4 normal, dry Mold Shrinkage 0.6 % ISO 294-4 parallel, dry Storage Temperature max. 140.0 °F Water Absorption 2.45 % ISO 62 at 23°C, dry, immersion, equilibrium - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 752.0 °F Lower Explosion Limit (SDS) 62.0 % at 85⁰C Melting Point (SDS) 360.0 °F - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr