Products

CYMEL® 1168 Resin is a highly monomeric, methylated/iso-butylated melamine crosslinker with a high degree of alkylation. Its high monomer content allows for the formulation of high solids coatings with excellent appearance, recoat adhesion, and flexibility. CYMEL® 1168 Resin is especially recommended for automotive topcoats, general metal finishes, and coil coatings. While CYMEL® 1168 Resin is insoluble in water, it shows excellent compatibility with water-soluble backbone polymers and provides very good stability in amine-stabilized waterborne formulations.

CYMEL® U-1051 is a partially iso-butylated urea resin supplied in a mixture of iso-butanol and xylene. It has wide compatibility with other film formers and is useful in fast curing industrial baking finishes and low temperature curing conversion varnishes.

CYMEL® 325 is a new type of highly methylated melamine-formaldehyde resin which does not require strong acid catalyst for fast cure response. CYMEL® 325 is reactive with hydroxyl amide and carboxyl group containing polymers. The weight loss of CYMEL® 325 during the baking process is significantly less than that of partially methylated melamine-formaldehyde resins. The baking volatiles from CYMEL® 325 contain very low levels of formaldehyde. The lower weight loss of CYMEL® 325 crosslinked coatings also results in less tendency to blister at higher film thickness. CYMEL® 325 requires only weak acid catalysis for cure; a low acid number in the backbone resin is suffi- cient. The cure reaction additionally can be catalyzed with weak organic acids or inorganic acids such as maleic, citric, phosphoric or alkyl phosphoric acids, low levels of p-toluene sulfonic acid or CYCAT® 14040 catalyst. CYMEL® 325 will self-condense like a partially methylated resin. Higher film hardness may, therefore, be obtained by raising the level of amino crosslinking agent. The high reaction rate of CYMEL® 325 at lower temperature reduces the chance of evaporation of low molecular weight resin components. CYMEL® 325 should, therefore, be very suitable for applications where "smoking" of the baking exhaust is a problem. Compared to partially methylated melamine-formalde- hyde resins, CYMEL® 325has shown, in some water-reducible coatings, improved humidity and salt- spray resistance. CYMEL 325 resin is FDA approved under section 121.2514 and 121.2526.

Dynasylan® VTMOEO is a bifunctional organosilane possessing a reactive vinyl group and a hydrolyzable 2­methoxy­ethoxy- silyl group.

Dynasylan® SILBOND® PURE functions as a surface modifier and crosslinking agent in CASE ingredients.

CYMEL® 327 resin is a methylated high imino melamine crosslinker supplied in isobutanol. CYMEL® 327 resin is very reactive and has a tendency towards selfcondensation at normal baking temperatures, providing films with very good hardness, gloss, chemical resistance and outdoor durability. Its major advantage relative to other high imino resins is its potential to lower VOC in high solids formulations.

Dynasylan® HYDROSIL 1151 is an amino-functional silane which acts as an adhesion promoter between inorganic materials (for example glass, metals and fillers) and organic polymers (thermosets, thermoplastics and elastomers). Dynasylan® HYDROSIL 1151 is a colorless to slightly yellowish aqueous solution with an amine-like odur, miscible, with alcohols or water. Dynasylan® HYDROSIL 1151 contains about 40% active silane content in water.

TRIGLYCIDYL ISOCYANURATE (TGIC) JF-77D is an isocyanurate based crystalline polyepoxide compound, its molecular weight is 297, it owns good heat resistance,weather resistance,adhesive and high temperature performance.

TRIGLYCIDYL ISOCYANURATE JF-77C is an isocyanurate-based crystalline polyepoxide compound, its molecular weight is 297 (CAS Number: 2451-62-9), and it owns good heat resistance, weather resistance, adhesive, and high-temperature performance.

CYMEL® MI-97-IX Resin is a partially iso-butylated melamine crosslinker supplied in a mixture of iso-butanol and xylene. Its fast drying behavior provides films with good early block resistance for stacking of parts and makes CYMEL® MI-97-IX Resin suitable for fast low temperature curing systems, like wood and paper coatings, providing very good film hardness, adhesion and appearance.

Dynasylan® HS2926 is a surface modifier, coupling agent, and crosslinking agent compatible with elastomers, rubbers, glass, metal, mineral substrates, thermoplastics, and thermosetting plastics. It functions as a coupling agent, crosslinking agent, and surface modifier in industrial additives.

CYMEL® 1133 Resin is a highly methylated, n-butylated melamine crosslinker with a high degree of alkylation. It has a higher butoxymethyl content and higher monomer content compared to CYMEL® 1130 resin. Its hydrophobic nature combined with very good film appearance properties makes CYMEL® 1133 resin suitable for automotive topcoat applications and general metal finishes requiring improved durability and resistance properties.

RHOPLEX® K-3 is an acrylic crosslinking agent.

Dynasylan® GLYMO is a bifunctional organosilane possessing a reactive organic epoxide and hydrolyzable inorganic methoxysilyl groups. The dual nature of its reactivity allows Dynasylan® GLYMO to bind chemically to both inorganic materials (e.g. glass, metals, fillers) and organic polymers (e.g. thermosets, thermoplastics, elastomers), thus functioning as an adhesion promoter, crosslinking agent and/or surface modifier. Dynasylan® GLYMO is a colorless low­viscosity liquid with a slight terpentine­like odor. It is soluble in alcohols, ketones and aliphatic or aromatic hydrocarbons.

Dynasylan® AMEO is a bifunctional silane possessing a reactive primary amino group and hydrolyzable ethoxysilyl groups. The dual nature of its reactivity allows Dynasylan® AMEO to bind chemically to both inorganic materials (e.g. glass, metals, fillers) and organic polymers (e.g. thermosets, thermoplastics, elastomers) thus functioning as an adhesion promoter, crosslinker, and/or surface modifier.