Features & Benefits
- Ready-to-Use Product Features
- Key Features and Benefits
- Product Features:
- Air dry curing process
- Excellent adhesion to many substrates,
- including aluminum, plastics and steel Water based coating
- Remains flexible over a wide range of temperatures
- Good release properties with a low coefficient of friction
- Product Benefits:
- Energy and processing savings
- Minimal pre-treatment required to achieve coating adhesion, thereby reducing processing costs
- Environmentally and people friendly resulting in compliance and worker satisfaction
- Application for a variety of environmental performance requirements
- Ability to meet lubrication and assembly requirements for the component and application
- Product Features:
Applications & Uses
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Cure Method
- Markets
- Applications
- Application and Usage Information
- Product Application:
- Paper handling mechanisms
- Nylon parts
- O-rings
- General hardware
- Usage Information
- Surface Preparation
- Substrates should be clean and dry. A chemical rinse or sandblast is usually sufficient to key the surface properly. However, if maximum adhesion is required, the combination of cleaning and surface pre-treatment by mechanical or chemical means is essential. Suggested methods of pre-treatment for maximum adhesion are as follows:
- Steel : degrease, sand or vapor blast and/or phosphate coat
- Stainless steel : degrease, sand or vapor blast
- Copper alloys : degrease, sand or vapor blast, dilute nitric acid drip, water rinse
- Aluminum : degrease, sand or vapor blast
- Rubber : degrease, using appropriate solvent
- Plastics : degrease, using appropriate solvent and/or light sanding
- Substrates should be clean and dry. A chemical rinse or sandblast is usually sufficient to key the surface properly. However, if maximum adhesion is required, the combination of cleaning and surface pre-treatment by mechanical or chemical means is essential. Suggested methods of pre-treatment for maximum adhesion are as follows:
- Mixing
- Stir to re-disperse solids that may have settled during storage. Avoid vigorous stirring which causes foaming. If dilution is necessary, blend four parts by weight BONDERITE® S-FN 8301 with one part by weight deionized water. If parts are to be dip coated, dilution may be necessary.
- Application
- Use an external atomizing spray gun with 35 to 50 psi (2-4 metric atmospheres) air pressure and adjust the gun to give a well-atomized spray. For optimum performance, the final coating thickness should be 0.0003-0.0007 inches (8-18 microns). When properly applied, the coating will be even and free of runs, blisters, or “fish eyes.” Close observation of color density will guide the experienced spray gun operator in obtaining even coverage.
- Spray
- Spray at 40 psi with fluid adjustment screw open 1/3 of a turn. Four passes yield a dry film thickness of 0.3-0.5 mils. Do not let material dry at gun tip. Keep material circulating at all times to avoid settling.
- Dip
- If coating thickness is too heavy when parts are coated at room temperature, dilute 10% with deionized water. If more than one coat is required, set coating 5 minutes at 93°C between dips.
- Cleanup
- Use water or alcohol/water blend. Dried coating may be cleaned with N-methyl-pyrrolidone.
- Drying
- Product can be air dried within 1-3 hours. Forced drying 10 minutes at 93-149°C is also possible.
- Surface Preparation
- Product Application:
Properties
- Physical Form
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000218
- Principal
Storage & Handling
- Storage and Shelf Life Information
- Shelf life for this product is 12 months from date of qualification under original seal. Do not store at temperatures above 35°C. Keep from freezing. Keep container tightly closed when not in use. Store in a cool, well ventilated area. Keep away from heat, sparks, and open flame. Protect material from direct sunlight. Ground and bond containers when transferring materials. Empty containers may retain hazardous properties.
Other
- Color
- Translucent
- Color (SDS)
- White
- IATA/ICAO Proper Shipping Name
- Not Applicable
- IATA/ICAO UN Number
- Not Applicable
- IMO/IMDG Proper Shipping Name
- Not Applicable
- IMO/IMDG UN Number
- Not Applicable
- Item Number
- Miscible in (SDS)
- Water
- Odor (SDS)
- Slight
- Protect from Freezing
- Yes
- Temperature Control
- Yes
- USA/DOT Proper Shipping Name
- Not Applicable
- USA/DOT UN Number
- Not Applicable
- Application Information
Value Units Test Method / Conditions Application Temperature 177.0 °C °C continuous - Material Composition
Value Units Test Method / Conditions Solid Content 25.0 % % by weight of wet product Volatile Organic Compounds (VOC) 325.0 g/L g/L of wet product - Mechanical Properties
Value Units Test Method / Conditions Coefficient of Friction 0.06 - as static Gloss 60.0-65.0 - at 60° angle - Physical Properties
Value Units Test Method / Conditions Coverage 7.82 m²/kg m²/kg at 25 μm dry film thickness, of wet product Density 1.07 kg/L kg/L Storage Temperature 41.0-86.0 °F °F - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Boiling Point (SDS) 100.0 °C °C Evaporation Rate (SDS) 1.0 % % Flash Point (SDS) 100.0 °C °C Pensky-Martens Closed Cup (PMCC) Melting Point (SDS) 0.0 °C °C Relative Vapor Density (SDS) 1.0 - Specific Gravity (SDS) 1.067 - Vapor Pressure (SDS) 17.0 mm Hg mm Hg Viscosity (SDS) 70.0 mPa.s mPa.s Volatile Organic Content (VOC) (SDS) 325.0 g/L g/L pH (SDS) 8.5 - - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 12.0 mo mo