Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM01672
- RTU Product Type
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Application Area
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Markets
- Applications
- Processing Information
Heat stability of acrylate comonomer allows processing temperatures as high as for polyesters (PBT, PET) and PPS.
CAUTION:
- LOTADER® AX8840 reacts with polymers containing maleic anhydride and acid. This reaction may generate gels and can block an extruder if not controlled. Extruders must be thoroughly purged before and after extrusion.
Properties
- Physical Form
Packaging & Availability
Storage & Handling
- Storage Conditions
- LOTADER® AX8840 should be stored in dry conditions and kept out of moisture in an aerated building. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging.
Other
- Appearance (SDS)
- Pellets
- Color (SDS)
- White translucent natural color
- Decomposition Temperature (SDS)
- min. 300.0 °C
- Density
- 0.94 g/cm³
- Density (SDS)
- 940.0 kg/m³
- Elongation at Break
- 400.0 %
- Elongation at Break
- 400.0 %
- Flexural Modulus
- 85.0 MPa
- Flexural Modulus
- 85.0 MPa
- Glycidyl Methacrylate Content
- 8.0 %(W/W)
- IATA/ICAO Proper Shipping Name
- Not Applicable
- IATA/ICAO UN Number
- Not Applicable
- IMO/IMDG Proper Shipping Name
- Not Applicable
- IMO/IMDG UN Number
- Not Applicable
- Insoluble in (SDS)
- Hydrocarbons, aromatic, halogenated, hot
- Item Number
- Melt Flow Index
- 5.0 g/10min
- Melt Flow Index
- 5.0 g/10min
- Melting Point
- 104.0 °C
- Melting Point (SDS)
- 104.0 °C
- Odor (SDS)
- Acrylic - like
- Other Hazards
- Contact with hot material - prevent serious burns. When heated to decomposition, emits toxic fumes. May be irritating to the respiratory system. The product is not biodegradable.
- Principal
- Shelf Life
- 3.0 yr
- Softening Point
- 87.0 °C
- Softening Point
- 87.0 °C
- Softening Point (SDS)
- 87.0 °C
- TDG Canada Proper Shipping Name
- Not Applicable
- TDG Canada UN Number
- Not Applicable
- Tensile Strength at Break
- 8.0 MPa
- Tensile Strength at Break
- 8.0 MPa
- USA/DOT Proper Shipping Name
- Not Applicable
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break1 400.0 % % ASTM D638 Elongation at Break2 400.0 % % ISO 527 Flexural Modulus3 85.0 MPa MPa ASTM D790 Flexural Modulus4 85.0 MPa MPa ISO 178 Tensile Strength at Break5 8.0 MPa MPa ASTM D638 Tensile Strength at Break 8.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Melt Flow Index 5.0 g/10min g/10min ASTM D1238 at 190°C, 2.16 kg Melt Flow Index 5.0 g/10min g/10min ISO 1133 at 190°C , 2.16 kg Melting Point 104.0 °C °C ISO 11357-3 Softening Point 87.0 °C °C ASTM D1525 10N Softening Point 87.0 °C °C ISO 306 10N - Material Composition
Value Units Test Method / Conditions Glycidyl Methacrylate Content 8.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 300.0 °C °C Density (SDS) 940.0 kg/m³ kg/m³ Melting Point (SDS) 104.0 °C °C Softening Point (SDS) 87.0 °C °C