Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM15354
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the methyl acrylate content, LOTRYL® 17BA07T can be used for applications where softness, flexibility, and polarity are required.
- LOTRYL® 17BA07T can be used as a tie layer in PP/PE coextrusion, in extrusion coating on many substrates, in compounds formulation, and foams.
- It is also suitable for wires and cables applications in HFFR formulations and SIOPLAST cross-linkable compound.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Compatible Substrates & Surfaces
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Technical Details & Test Data
- Processing Details
LOTRYL® 17BA07T can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 17BA07T is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 17BA07T should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- Protect from Freezing
- Yes
- Temperature Control
- Yes
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Butyl Acrylate Content 17.0 - Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 800.0 - ASTM D638 Elongation at Break 800.0 - ISO 527-2 Flexural Modulus 74.0 MPa MPa ASTM D790 Flexural Modulus 74.0 MPa MPa ISO 178 Hardness 93.0 - Hardness 93.0 - ASTM D2240 Hardness 93.0 - ISO 868 Tensile Strength at Break 11.0 MPa MPa ASTM D638 Tensile Strength at Break 11.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ISO 1193 Melt Flow Index 7.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 7.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 107.0 °C °C ISO 11357-3 Softening Point 65.0 °C °C ASTM D1525 at 10N Softening Point 65.0 °C °C ISO 306 at 10N Softening Point 65.0 °C °C Vicat Softening Point Test at 10N Storage Temperature max. 86.0 °F °F - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) approx. 662.0 °C °C Bulk Density (SDS) approx. 500.0 - At 68°F Decomposition Temperature (SDS) min. 662.0 °F °F Density (SDS) 920.0-980.0 - at 68°F Melting Point (SDS) 140.0-212.0 °F °F - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 -