Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Chemical Name
- Plastics & Elastomers Functions
- Product Code
- MITM01696
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the methyl acrylate content, LOTRYL® 24MA005 can be used for applications where softness, flexibility, and polarity are required.
- Typical applications are extrusion coating, co-extrusion, and compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Compatible Substrates & Surfaces
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Technical Details & Test Data
- Processing Details
LOTRYL® 24MA005 can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 24MA005 is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 24MA005 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness . (severity of effects depends on extent of exposure) , Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- Protect from Freezing
- Yes
- Temperature Control
- Yes
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 24.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 750.0 % % ASTM D638 Elongation at Break 750.0 % % ISO 527-2 Flexural Modulus 18.0 MPa MPa ASTM D790 Flexural Modulus 18.0 MPa MPa ISO 178 Tensile Strength at Break 17.0 MPa MPa ASTM D638 Tensile Strength at Break 17.0 MPa MPa ISO 527 Tensile Strength at Break 17.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ISO 1193 Melt Flow Index 0.5 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 0.5 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 72.0 °C °C ISO 11357-3 Softening Point 45.0 °C °C ASTM D1525 at 10N Softening Point 45.0 °C °C ISO 306 at 10N Softening Point 45.0 °C °C Vicat Softening Point Test at 10N Storage Temperature max. 86.0 °F °F - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) approx. 662.0 °F °F Bulk Density (SDS) approx. 500.0 kg/m³ kg/m³ At 68°F Decomposition Temperature (SDS) min. 662.0 °F °F Density (SDS) 0.94 g/cm³ g/cm³ at 68°F Melting Point (SDS) 162.0 °F °F - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr