Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM16120
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the methyl acrylate content, LOTRYL® 24MA02 can be used for applications where softness, flexibility, and polarity are required.
- Typical applications are extrusion coating, co-extrusion, and compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Processing Details
LOTRYL® 24MA02 can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 24MA02 is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 24MA02 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 800.0 % % ASTM D638 Elongation at Break 800.0 % % ISO 527-2 Flexural Modulus 18.0 MPa MPa ASTM D790 Flexural Modulus 18.0 MPa MPa ISO 178 Hardness 79.0 Shore D Shore D Hardness 79.0 HV HV ASTM D2240 Hardness 79.0 Shore D Shore D ASTM D2240 Hardness 79.0 HV HV ISO 868 Hardness 79.0 Shore D Shore D ISO 868 Tensile Strength at Break 12.0 MPa MPa ASTM D638 Tensile Strength at Break 12.0 MPa MPa ISO 527 Tensile Strength at Break 12.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ISO 1193 Melt Flow Index 2.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 2.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 68.0 °C °C ISO 11357-3 Softening Point 49.0 °C °C ASTM D1525 at 10N Softening Point 49.0 °C °C ISO 306 at 10N Softening Point 49.0 °C °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 24.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 350.0 °C °C Density (SDS) 900.0-950.0 kg/m³ kg/m³ Melting Point (SDS) max. 80.0 °C °C