Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the high methyl acrylate content, LOTRYL® 24MA07T can be used for applications where softness, flexibility, and polarity are required.
- Typical applications are flexible film, polyesters modification, masterbatch carrier resin, and cable compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Compatible Substrates & Surfaces
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Technical Details & Test Data
- Processing Details
LOTRYL® 24MA07T can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 24MA07T is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 24MA07T should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- Temperature Control
- Yes
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 24.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break max. 500.0 % % ASTM D638 Elongation at Break max. 500.0 % % ISO 527-2 Flexural Modulus 36.0 MPa MPa ASTM D790 Flexural Modulus 36.0 MPa MPa ISO 178 Hardness 78.0 Shore A Shore A Hardness 78.0 Shore A Shore A ASTM D2240 Hardness 78.0 Shore A Shore A ISO 868 Tensile Strength 5.0 MPa MPa ASTM D638 at 500% Tensile Strength 5.0 MPa MPa ISO 527-2 at 500% Tensile Strength at Break 5.0 MPa MPa ASTM D638 Tensile Strength at Break 5.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.95 g/cm³ g/cm³ ASTM D150 Density 0.95 g/cm³ g/cm³ ISO 1193 Melt Flow Index 7.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 7.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 97.0 °C °C ISO 11357-3 Softening Point 49.0 °C °C ASTM D1525 at 10N Softening Point 49.0 °C °C ISO 306 at 10N Softening Point 49.0 °C °C Vicat Softening Point Test at 10N Storage Temperature max. 86.0 °F °F - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) approx. 662.0 °F °F ASTM D1929 Bulk Density (SDS) approx. 500.0 kg/m³ kg/m³ At 68°F Decomposition Temperature (SDS) 350.0-662.0 °F °F Density (SDS) 920.0-980.0 kg/m³ kg/m³ at 68°F Melting Point (SDS) 140.0-212.0 °F °F - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr