Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the high butyl acrylate content, LOTRYL® 28BA700T can be used for applications where flexibility and polarity are required.
- Thanks to its high fluidity, LOTRYL® 28BA700T is suitable for the formulation of hot melt adhesives.
- It can also be used as a processing-aid in highly filled compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Technical Details & Test Data
- Processing Details
LOTRYL® 28BA700T can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 28BA700T should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product. Due to its physical properties, it may be possible that the LOTRYL® 28BA700T shows some caking. This is particularly true during summer time.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Color (SDS)
- Translucent
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- Protect from Freezing
- Yes
- Temperature Control
- Yes
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Butyl Acrylate Content 28.0 - Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Flexural Modulus max. 10.0 MPa MPa ASTM D790 Flexural Modulus max. 10.0 MPa MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ISO 1193 Melt Flow Index 700.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 700.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 94.0 °C °C ISO 11357-3 Softening Point 100.0 °C °C Ring and Ball Test Softening Point max. 40.0 °C °C ASTM D1525 at 10N Softening Point 100.0 °C °C ASTM E28 Softening Point max. 40.0 °C °C ISO 306 at 10N Softening Point max. 40.0 °C °C Vicat Softening Point Test at 10N Storage Temperature max. 86.0 °F °F - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Bulk Density (SDS) approx. 500.0 - at 20°C Decomposition Temperature (SDS) 662.0 °F °F Density (SDS) 0.92-0.98 g/cm³ g/cm³ at 20°C Melting Point (SDS) 185.0-239.0 °F °F Specific Gravity (SDS) 0.92-0.98 - at 23°C, liquid, water = 1 - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 -