Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the methyl acrylate content, LOTRYL® 29MA03 can be used for applications where softness, flexibility, and polarity are required.
- Typical applications are extrusion coating, co-extrusion, and compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Processing Details
LOTRYL® 29MA03 can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 29MA03 is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 29MA03 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Due to its physical properties (Vicat temperature <40°C), it may be possible that the product shows some caking. This is particularly true during summer time.
- Three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester-like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 900.0 % ASTM D638 Elongation at Break 900.0 % ISO 527-2 Flexural Modulus 10.0 MPa ASTM D790 Flexural Modulus 10.0 MPa ISO 178 Hardness 75.0 Shore A Hardness 75.0 Shore A ASTM D2240 Hardness 75.0 Shore A ISO 868 Tensile Strength at Break 6.0 MPa ASTM D638 Tensile Strength at Break 6.0 MPa ISO 527 Tensile Strength at Break 6.0 MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ ASTM D150 Density 0.94 g/cm³ ISO 1193 Melt Flow Index 3.0 g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 3.0 g/10min ISO 1133 at 190°C, 2.16kg Melting Point 61.0 °C ISO 11357-3 Softening Point max. 40.0 °C ASTM D1525 at 10N Softening Point max. 40.0 °C ISO 306 at 10N Softening Point max. 40.0 °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 29.0 %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Bulk Density (SDS) approx. 500.0 kg/m³ at 20°C Decomposition Temperature (SDS) min. 662.0 °F Density (SDS) 0.95 g/cm³ at 20°C Melting Point (SDS) 142.0 °F Specific Gravity (SDS) 0.95 - liquid