Enhanced TDS
Identification & Functionality
- Blend
- No
- CASE Ingredients Functions
- Chemical Family
- Chemical Name
- Plastics & Elastomers Functions
- Product Code
- MITM01705
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the high butyl acrylate content, LOTRYL® 35BA320 can be used for applications where flexibility and polarity are required.
- Combined with a high fluidity, LOTRYL® 35BA320 is particularly recommended for the formulation of hot melt adhesives.
- It can also be used as a processing-aid in highly filled compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Processing Details
LOTRYL® 35BA320 can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 35BA320 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Due to its physical properties (Vicat temperature <40°C), it may be possible that the LOTRYL® 35BA320 shows some caking. This is particularly true during summer time.
- Shelf Life: Three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure), Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 200.0 % ASTM D638 Elongation at Break 200.0 % ISO 527-2 Flexural Modulus max. 10.0 MPa ASTM D790 Flexural Modulus max. 10.0 MPa ISO 178 Hardness 52.0 Shore A Hardness 52.0 Shore A ASTM D2240 Hardness 52.0 Shore A ISO 868 Tensile Strength at Break 2.0 MPa ASTM D638 Tensile Strength at Break 2.0 MPa ISO 527 Tensile Strength at Break 2.0 MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ ASTM D150 Density 0.94 g/cm³ ISO 1193 Melt Flow Index 320.0 g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 320.0 g/10min ISO 1133 at 190°C, 2.16kg Melting Point 65.0 °C ISO 11357-3 Softening Point 85.0 °C Ring and Ball Test Softening Point max. 40.0 °C ASTM D1525 at 10N Softening Point 85.0 °C ASTM E28 Softening Point max. 40.0 °C ISO 306 at 10N Softening Point max. 40.0 °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Butyl Acrylate Content 35.0 %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) approx. 662.0 °F Bulk Density (SDS) 500.0 kg/m³ At 68°F Decomposition Temperature (SDS) approx. 662.0 °F Density (SDS) 0.93 g/cm³ Melting Point (SDS) 149.0 °F