Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Chemical Name
- EC Number
- 607-803-0
- Plastics & Elastomers Functions
- Product Code
- MITM13397
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the high butyl acrylate content, LOTRYL® 35BA320T can be used for applications where flexibility and polarity are required.
- Thanks to its high fluidity, LOTRYL® 35BA320T is suitable for the formulation of hot melt adhesives.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Processing Details
LOTRYL® 35BA320T can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 35BA320T should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Due to its physical properties, it may be possible that the LOTRYL® 35BA320T shows some caking. This is particularly true during summer time.
- Shelf Life: Three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- Translucent
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 110.0 % ASTM D638 Elongation at Break 110.0 % ISO 527-2 Flexural Modulus max. 10.0 MPa ASTM D790 Flexural Modulus max. 10.0 MPa ISO 178 Hardness 54.0 Shore A Hardness 54.0 Shore A ASTM D2240 Hardness 54.0 Shore A ISO 868 Tensile Strength at Break 1.3 MPa ASTM D638 Tensile Strength at Break 1.3 MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ ASTM D150 Density 0.94 g/cm³ ISO 1193 Melt Flow Index 320.0 g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 320.0 g/10min ISO 1133 at 190°C, 2.16kg Melting Point 90.0 °C ISO 11357-3 Softening Point 102.0 °C Ring and Ball Test Softening Point max. 40.0 °C ASTM D1525 at 10N Softening Point 102.0 °C ASTM E28 Softening Point max. 40.0 °C ISO 306 at 10N Softening Point max. 40.0 °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Butyl Acrylate Content 35.0 %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 662.0 °F Bulk Density (SDS) 500.0 kg/m³ At 68°F Decomposition Temperature (SDS) min. 662.0 °F Density (SDS) 0.92-0.98 g/cm³ at 68°F Melting Point (SDS) 140.0-212.0 °F Specific Gravity (SDS) 0.92-0.98 - at 73°F, liquid, water=1