Enhanced TDS
Identification & Functionality
- Blend
- No
- CASE Ingredients Functions
- Chemical Family
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM01712
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Used as top layer of laminates in order to provide the functions of heat sealability onto various substrates like PP, PS, PET and PVC, and easy opening by interfacial peeling.
- Easily processed using the technologies of coextrusion coating, cast film coextrusion, blown film coextrusion or sheet coextrusion, to produce multilayers that can be used as lids, directly or after lamination with other films.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Compatible Substrates & Surfaces
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Technical Details & Test Data
- Processing Details
- LOTRYL® BESTPEEL 2407 can be used as a peelable heat seal layer in many kinds of lid constructions, based on aluminium foil, plastic films, paper, or a combination of them.
- Structure examples:
- Reverse printed bi-oriented film / adhesive / LDPE / BESTPEEL 2407
- Aluminium / adhesive / LDPE / BESTPEEL 2407
- Such constructions are heat sealable onto PP, PS, APET, and PVC.
- Sealing strength is dependent on factors related to the different materials involved (heat conductivity, thicknesses) and technological parameters like shape of the sealing tools, actual pressure, and time.
- As general recommendations, flat sealing bars and moderate pressure should be preferred for better results and less squeezing of the sealing layer.
- Sealing temperature should be in the range from 160-180°C to 220-240°C, depending on heat conductivity of the whole structure and on contact time.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® BESTPEEL 2407 should be stored in standard conditions and protected from UV- light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure), Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 1095.0 d d - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 800.0 % % ASTM D638 Elongation at Break 800.0 % % ISO 527-2 Flexural Modulus 14.0 MPa MPa ASTM D790 Flexural Modulus 14.0 MPa MPa ISO 178 Hardness 79.0 Shore A Shore A Hardness 79.0 Shore A Shore A ASTM D2240 Hardness 79.0 Shore A Shore A ISO 868 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ISO 1193 Melt Flow Index 2.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 2.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 69.0 °C °C ISO 11357-3 Softening Point max. 40.0 °C °C ASTM D1525 at 10N Softening Point max. 40.0 °C °C ISO 306 at 10N Softening Point max. 40.0 °C °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 23.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) approx. 662.0 °F °F Bulk Density (SDS) approx. 500.0 kg/m³ kg/m³ At 68°F Decomposition Temperature (SDS) min. 662.0 °F °F Density (SDS) 0.94 g/cm³ g/cm³ at 68°F Melting Point (SDS) 156.0 °F °F