Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM01734
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
- Key Features
- OREVAC® 18507 has been designed to be used as coupling agent in halogen free flame retardant cable compounds. It provides outstanding mechanical properties, high tensile strength at break and good elongation, good abrasion and good chemical resistance.
- OREVAC® 18507 is suitable also to develop a reliable bonding strength between HDPE resins and mineral filler or natural fibers. Desianed to develop a reliable bonding between polyethylene or most ethylene copolymers and many kinds of different materials among which polyamides and EVOH.
Applications & Uses
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
Properties
- Physical Form
Technical Details & Test Data
- Processing Parameters
OREVAC® 18507 is suitable for the production of compounds with the most common types of equipments (internal mixer, Büss®, kneader, twin screw extruder); it provides an effectivecoupling between the base polymers, mineral fillers (ATH, MDH), and natural fibers.
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage Conditions
- OREVAC® 18507 should be stored in dry conditions protected from UV-light.
- Improper storage conditions may cause degradation and have consequences on physical properties of the product.
- Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Bulk Density (SDS)
- 500.0 kg/m³
- Color (SDS)
- White
- Decomposition Temperature (SDS)
- min. 280.0 °C
- Density
- 0.95 g/cm³
- Density
- 0.95 g/cm³
- Density (SDS)
- 900.0-950.0 kg/m³
- Hardness
- 66.0 HV
- Hardness
- 66.0 Shore D
- Hardness
- 66.0 HV
- Insoluble in (SDS)
- Water
- Item Number
- Melt Flow Index
- 5.0 g/10min
- Melt Flow Index
- 5.0 g/10min
- Melting Point
- 128.0 °C
- Melting Point (SDS)
- 90.0-140.0 °C
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation., The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases: Irritating to eyes, respiratory system and skin. Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- Principal
- Shelf Life
- 3.0 yr
- Tensile Strength at Break
- 10.0 MPa
- Tensile Strength at Break
- 10.0 MPa
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Hardness1 66.0 HV HV ASTM D2240 Hardness2 66.0 Shore D Shore D Shore Durometer Scale Hardness3 66.0 HV HV ISO 868 Tensile Strength at Break4 10.0 MPa MPa ASTM D638 Tensile Strength at Break 10.0 MPa MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density 0.95 g/cm³ g/cm³ ISO 1183 Density 0.95 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 5.0 g/10min g/10min ASTM D1238 at 190°C, 2.16 kg Melt Flow Index 5.0 g/10min g/10min ISO 1133 at 190°C , 2.16 kg Melting Point 128.0 °C °C ISO 11357-3 - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Bulk Density (SDS) 500.0 kg/m³ kg/m³ Decomposition Temperature (SDS) min. 280.0 °C °C Density (SDS) 900.0-950.0 kg/m³ kg/m³ at 20°C Melting Point (SDS) 90.0-140.0 °C °C