Enhanced TDS
Identification & Functionality
- Additives Included
- Blend
- Yes
- Chemical Family
- Country of Origin
- Function
- Anti-Static Agent
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM01791
- Single Ingredient
- No
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
- Processing Information
- Injection Molding
- Film Extrusion
- Profile Extrusion
- Extrusion
- Transfer Molding
- Casting
- Thermoforming
- Processing Information
- Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.
- Typical mold temperature: 25–60°C.
- Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.
Properties
Technical Details & Test Data
- Technical Data
Viscosity-shear Rate
Shearstress-shear Rate
Stress-strain
Secant Modulus-strain
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000003
- Principal
Other
- Color (SDS)
- Colorless to slightly yellow
- Insoluble in (SDS)
- Water
- Item Number
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Electrical Properties
Value Units Test Method / Conditions Dielectric Strength 5.0 kV/mm kV/mm IEC 60243-1 dry basis Surface Resistance 3000000000.0 Ω Ω IEC 60093 condensed Volume Resistivity 25000000.0 Ω-cm Ω-cm IEC 60093 condensed Volume Resistivity 1500000000.0 Ω-cm Ω-cm IEC 60093 dry basis - Mechanical Properties
Value Units Test Method / Conditions Hardness 40.0 Shore A Shore A ISO 868 Strain max. 700.0 % % ISO 527 normal, dry Strain max. 500.0 % % ISO 527 parallel, dry Strain at Break min. 50.0 % % ISO 527-1 Dry, at break Strain at Break min. 300.0 % % ISO 527-1 dry, thermoplastic elastomer, at break Strain at Break min. 50.0 % % ISO 527-2 at break, condensed Stress 10.0 MPa MPa ISO 527-1 dry, at 50% strain Stress 10.0 MPa MPa ISO 527-2 condensed, at 50% strain Stress max. 34.0 MPa MPa ISO 527 normal, dry Stress max. 32.0 MPa MPa ISO 527 parallel, dry Stress at Break 30.0 MPa MPa ISO 527-1 dry, thermoplastic elastomer, at break Tensile Modulus 97.0 MPa MPa ISO 527-1 dry basis Tensile Modulus 80.0 MPa MPa ISO 527-2 condensed - Physical Properties
Value Units Test Method / Conditions Density 1070.0 kg/m³ kg/m³ ISO 1183 dry basis Glass Transition Temperature (Tg) -40.0 °C °C ISO 11357-1 at 10°C/min, dry Humidity Absorption 1.4 % % ISO 62 Melting Point 158.0 °C °C ISO 11357-1 at 10°C/min Storage Temperature max. 140.0 °F °F Water Absorption 48.0 % % ISO 62 dry basis - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 788.0-842.0 °F °F Decomposition Temperature (SDS) 300.0-350.0 °C °C Melting Point (SDS) 158.0-172.0 °C °C