Enhanced TDS
Identification & Functionality
- Additives Included
- Blend
- Yes
- Chemical Family
- Function
- Anti-Static Agent
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM01792
- Single Ingredient
- No
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Packaging & Availability
- Packaging Type
- Product Packaging
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.
Other
- Application Temperature
- 65.0-75.0 °C
- Application Temperature
- 25.0-60.0 °C
- Autoignition Temperature (SDS)
- 788.0-842.0 °F
- Charge Decay
- max. 1.0 s
- Color (SDS)
- White to slightly yellow
- Decomposition Temperature (SDS)
- 572.0-662.0 °F
- Density
- 1.07 g/cm³
- Drying Time
- 4.0-6.0 hr
- Flexural Modulus
- 80.0 MPa
- Hardness
- 40.0 Shore A
- Insoluble in (SDS)
- Water
- Melting Point
- 210.0-230.0 °C
- Melting Point
- 200.0-270.0 °C
- Melting Point
- 160.0 °C
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation., Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- Principal
- Refractive Index
- 1.502
- Shelf Life
- 2.0 yr
- Strain at Break
- min. 700.0 %
- Stress at Break
- 30.0 MPa
- Surface Resistivity
- 10000000.0 Ω/sq
- Volume Resistivity
- 10000000.0 Ω-cm
- Water Absorption
- 1.4 %
- Water Absorption
- 48.0 %
- Optical Properties
Value Units Test Method / Conditions Refractive Index 1.502 - Internal Method - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Electrical Properties
Value Units Test Method / Conditions Charge Decay max. 1.0 s s MIL-B-81705 at 23°C, 50% R.H., 15 days Surface Resistivity 10000000.0 Ω/sq Ω/sq IEC 60093 at 23°C, 50% R.H., 15 days Volume Resistivity 10000000.0 Ω-cm Ω-cm IEC 60093 at 23°C, 50% R.H, 15 days - Mechanical Properties
Value Units Test Method / Conditions Flexural Modulus 80.0 MPa MPa ISO 178 at 23°C, 50% R.H., 15 days Hardness 40.0 Shore A Shore A ISO 868 at 23°C, 50% R.H, 1MHz, instantaneous Strain at Break min. 700.0 % % ISO 527 at 23°C, 50% R.H., 15 days, at break Stress at Break 30.0 MPa MPa ISO 527 at 23°C, 50% R.H., 15 days, at break - Physical Properties
Value Units Test Method / Conditions Density 1.07 g/cm³ g/cm³ ISO 1183 Drying Time 4.0-6.0 hr hr drying, bags opened for more than 2 hours Melting Point 210.0-230.0 °C °C extrusion Melting Point 200.0-270.0 °C °C injection Melting Point 160.0 °C °C ISO 11357 Water Absorption 1.4 % % ISO 62 at 20°C, 50% RH, at equilibrium Water Absorption 48.0 % % ISO 62 at 23°C, 24 hr in water - Application Information
Value Units Test Method / Conditions Application Temperature 65.0-75.0 °C °C drying, bags opened for more than 2 hours Application Temperature 25.0-60.0 °C °C mold - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 788.0-842.0 °F °F Decomposition Temperature (SDS) 572.0-662.0 °F °F