Enhanced TDS
Identification & Functionality
- Additives Included
- Blend
- Yes
- Chemical Family
- Polymer Name
- Product Code
- MITM14903
- Single Ingredient
- No
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Processing Information
Injection Molding, Film Extrusion, Profile Extrusion, Other Extrusion, Transfer Molding, Casting, Thermoforming.
Properties
Technical Details & Test Data
- Technical Data
Stress-Strain Diagram:
Secant Modulus-Strain Diagram:
Processing Conditions:
- Typical melt temperature (Min / Recommended / Max): 230°C / 260°C / 290°C.
- Typical mold temperature: 25 - 60°C.
- Drying time and temperature (only necessary for bags opened for more than two hours): 5-7 hours at 70-80°C.
Processing Conditions:
- Typical melt temperature (Min / Recommended / Max): 230°C / 260°C / 290°C.
- Drying time and temperature (only necessary for bags opened for more than two hours): 5-7 hours at 70-80°C.
Packaging & Availability
- Packaging Type
- Product Packaging
PEBAX® Rnew® 72R53 SP 01 is delivered dried in sealed packaging (20 kg bags) ready to be processed.
Other
- Autoignition Temperature (SDS)
- 698.0-842.0 °F
- Bulk Density (SDS)
- 550.0-650.0 kg/m³
- Carbon Content
- 90.0 %
- Charpy Impact Strength
- 13.0 kJ/m²
- Color (SDS)
- Colorless to slightly yellow
- Decomposition Temperature (SDS)
- 572.0-662.0 °F
- Density
- 1030.0 kg/m³
- Density
- 1030.0 kg/m³
- Density (SDS)
- 1.03 g/cm³
- Hardness
- 65.0 Shore D
- Hardness
- 65.0 Shore A
- Humidity Absorption
- 0.8 %
- Item Number
- Lower Explosion Limit (SDS)
- 90.0 %
- Melting Point
- 186.0 °C
- Melting Point (SDS)
- 367.0 °F
- Mold Shrinkage
- 1.3 %
- Mold Shrinkage
- 1.5 %
- Mold Shrinkage
- 1.3 %
- Mold Shrinkage
- 1.5 %
- Nominal Strain at Break
- min. 50.0 %
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation., Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- Principal
- Shelf Life
- 2.0 yr
- Softening Point
- 175.0 °C
- Solubility In Water (SDS)
- max. 1.0 mg/L
- Strain at Break
- min. 300.0 %
- Strain at Yield
- 28.0 %
- Stress
- 57.0 MPa
- Stress at Yield
- 28.0 MPa
- Tensile Modulus
- 560.0 MPa
- Water Absorption
- 0.7 %
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 13.0 kJ/m² kJ/m² ISO 179-1EA at -30°C, condensed, notched Hardness 65.0 Shore D Shore D Hardness 65.0 Shore A Shore A ISO 868 Nominal Strain at Break min. 50.0 % % ISO 527-2 at break, condensed, nominal Strain at Break min. 300.0 % % ISO 527-1 at break thermoplastic elastomer, dry Strain at Yield 28.0 % % ISO 527-2 condensed Stress 57.0 MPa MPa ISO 527-1 at 300% elongation, dry Stress at Yield 28.0 MPa MPa ISO 527-2 condensed, at yield Tensile Modulus 560.0 MPa MPa ISO 527-2 condensed - Physical Properties
Value Units Test Method / Conditions Density 1030.0 kg/m³ kg/m³ ISO 1183 condensed Density 1030.0 kg/m³ kg/m³ ISO 1183 Dry Humidity Absorption 0.8 % % ISO 62 Dry Melting Point 186.0 °C °C ISO 11357-1 at 10°C/min Mold Shrinkage 1.3 % % ISO 2577 normal, dry Mold Shrinkage 1.5 % % ISO 2577 parallel, dry Mold Shrinkage 1.3 % % ISO 294-4 normal, dry Mold Shrinkage 1.5 % % ISO 294-4 parallel, dry Softening Point 175.0 °C °C ISO 306 at 50°C/h, 50N, dry Water Absorption 0.7 % % ISO 62 Dry - Material Composition
Value Units Test Method / Conditions Carbon Content 90.0 % % ASTM D6866 - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 698.0-842.0 °F °F Bulk Density (SDS) 550.0-650.0 kg/m³ kg/m³ Decomposition Temperature (SDS) 572.0-662.0 °F °F Density (SDS) 1.03 g/cm³ g/cm³ Lower Explosion Limit (SDS) 90.0 % % at 85⁰C Melting Point (SDS) 367.0 °F °F Solubility In Water (SDS) max. 1.0 mg/L mg/L at 20°C