Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM09985
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Labeling Claims
- Materials Features
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Plastics & Elastomers Processing Methods
- Processing Information
- As a result of high-pressure polymerization in autoclave reactor, LOTADER® 4403 molecular structure and rheology are remarkably suitable for all kinds of extrusion, including extrusion coating/lamination: low neck-in, excellent melt stability and drawability.
- Standard polyolefin extrusion equipment can be used for LOTADER® 4403, which has the same processability as LDPE and the same heat stability given by acrylate comonomers. Recommended temperature range is from 270°C up to 320 – 330°C. It is recommended to purge the equipment with LDPE after a run is completed before shutting down.
- Product Applications
LOTADER® 4403 is a versatile adhesive resin for extrusion lamination/coating, not intended to be diluted. LOTADER® 4403 provides excellent adhesion to various substrates in extrusion lamination process. It bonds to PE, paper, board, metallized films and corona treated PE, OPP, CPP and OPA films.
Typical applications:
- Adhesive for extrusion coating lamination: Film / Tie / Foil.
- Adhesive for extrusion coating of LDPE / Tie / PA / Tie onto paper or films.
Properties
- Physical Form
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTADER® 4403 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Shelf life is two years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure), Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- Temperature Control
- Yes
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Acrylate Content 18.0 - Internal Method C12/C14 Maleic Anhydride Content 0.3 - Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 750.0 - ASTM D638 Elongation at Break 750.0 - ISO 527 Flexural Modulus 20.0 MPa MPa ASTM D790 Flexural Modulus 20.0 MPa MPa ISO 178 Hardness 25.0 - Shore Durometer Scale Tensile Strength at Break 9.0 MPa MPa ASTM D638 Tensile Strength at Break 9.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ISO 1183 Density 0.94 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 8.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 8.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 77.0 °C °C ISO 11357-3 Softening Point 45.0 °C °C ASTM D1525 Softening Point 45.0 °C °C ISO 306 Storage Temperature max. 122.0 °F °F - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 842.0 °F °F Decomposition Temperature (SDS) min. 572.0 °F °F Density (SDS) 950.0 - at 68°F Melting Point (SDS) 176.0-203.0 °F °F - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 -