Identification & Functionality
- Blend
- No
- Chemical Family
- Chemical Name
- Plastics & Elastomers Functions
- Product Code
- MITM01667
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Compatible Polymers & Resins
- Processing Information
Heat stability of acrylate comonomer allows processing temperatures as high as for polyamides. However, to minimize the generation of gels, it is recommended to purge the equipment with LDPE after a run is completed. LOTADER® 4720 is not corrosive.
Properties
- Physical Form
- Soluble In
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTADER® 4720 is usually packed in waterproof bags or rigid containers with waterproof liner. It should be stored in dry conditions and be kept out of moisture in an aerated building.
- Improper storage conditions may cause degradation and could have consequences on physical properties of the product. It is recommended to reseal the bag or the liner after use to protect LOTADER® 4720 against moisture.
- Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- Colorless
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Slightly acrylic
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 800.0 % % ASTM D638 Elongation at Break 800.0 % % ISO 527 Flexural Modulus max. 30.0 MPa MPa ASTM D790 Flexural Modulus max. 30.0 MPa MPa ISO 178 Tensile Strength at Break 5.0 MPa MPa ASTM D638 Tensile Strength at Break 5.0 MPa MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ISO 1183 Density 0.94 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 7.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 7.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 65.0 °C °C ISO 11357-3 Softening Point 154.0 °C °C Ring and Ball Test Softening Point max. 40.0 °C °C ASTM D1525 10N Softening Point 154.0 °C °C ASTM E28 Softening Point max. 40.0 °C °C ISO 306 10N - Material Composition
Value Units Test Method / Conditions Ethyl Acrylate Content 29.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) Maleic Anhydride Content 0.3 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 842.0 °F °F Bulk Density (SDS) 500.0 kg/m³ kg/m³ Decomposition Temperature (SDS) min. 572.0 °F °F Density (SDS) 940.0 kg/m³ kg/m³ at 68°F Melting Point (SDS) 149.0 °F °F