LOTADER® 9305T can be processed on most conventional equipment used for thermoplastics. It is recommended to avoid overheating above 230°C and to purge the equipment after a run is completed.
Properties
- Physical Form
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage Conditions
- LOTADER® 9305T should be stored in dry conditions protected from UV-light. Improper storage conditions may cause degradation and have consequences on physical properties of the product.
- Due to its physical properties (Vicat temperature <40°C), it may be possible that the product shows some caking.
- This is particularly true during summer time. Three years from the date of delivery, in unopened packaging.
Other
- Appearance (SDS)
- Pellet
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester
- Other Hazards
- Contact with hot material - prevent serious burns. May be irritating to the respiratory system. The product is not biodegradable.
- Protect from Freezing
- No
- Temperature Control
- No
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Maleic Anhydride Content 6400.0 ppm ppm Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 800.0 - ASTM D638 Elongation at Break 800.0 - ISO 527 Hardness 75.0 HV HV ASTM D2240 Hardness 75.0 - Shore Durometer Scale Hardness 75.0 HV HV ISO 868 Tensile Strength at Break 5.5 MPa MPa ASTM D638 Tensile Strength at Break 5.5 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ISO 1183 Density 0.94 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 180.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 180.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 68.0 °C °C ISO 11357-3 Softening Point 92.0 °C °C Ring and Ball Test Softening Point max. 40.0 °C °C ASTM D1525 10N Softening Point 92.0 °C °C ASTM E28 Softening Point max. 40.0 °C °C ISO 306 10N - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 350.0 °C °C Decomposition Temperature (SDS) min. 260.0 °C °C Density (SDS) 940.0 - Melting Point (SDS) 65.0-70.0 °C °C DIN 51007 Melting Point (SDS) 65.0-70.0 °C °C Differential Scanning Calorimetry Melting Point (SDS) 65.0-70.0 °C °C Differential Thermal Analysis Relative Density (SDS) 0.93-0.955 - at 20°C - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 -