Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the methyl acrylate content, LOTRYL® 28MA07 can be used for applications where softness, flexibility, and polarity are required.
- Typical applications are extrusion coating, co-extrusion, and compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Technical Details & Test Data
- Processing Details
- LOTRYL® 28MA07 can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 28MA07 is used pure for instance with blown or cast film technology, standard temperature settings could be:
- Final profile and settings depend on the line and multilayer structure being run.
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 28MA07 should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product.
- Due to its physical properties (Vicat temperature <40°C), it may be possible that the product shows some caking. This is particularly true during summer time.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- ADR/RID/ADN Proper Shipping Name
- Not Applicable
- ADR/RID/ADN UN Number
- Not Applicable
- Appearance (SDS)
- Pellet
- Color (SDS)
- Natural color
- IATA/ICAO Proper Shipping Name
- Not Applicable
- IATA/ICAO UN Number
- Not Applicable
- IMO/IMDG Proper Shipping Name
- Not Applicable
- IMO/IMDG UN Number
- Not Applicable
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester
- Other Hazards
- Contact with hot material - prevent serious burns. When heated to decomposition, emits toxic fumes. May be irritating to the respiratory system. May cause slight irritation to eyes. The product is not biodegradable.
- Protect from Freezing
- Yes
- Temperature Control
- Yes
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Methyl Acrylate Content 28.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 900.0 % % ASTM D638 Elongation at Break 900.0 % % ISO 527-2 Flexural Modulus 10.0 MPa MPa ASTM D790 Flexural Modulus 10.0 MPa MPa ISO 178 Hardness 76.0 Shore A Shore A Hardness 76.0 Shore A Shore A ASTM D2240 Hardness 76.0 Shore A Shore A ISO 868 Tensile Strength at Break 7.0 MPa MPa ASTM D638 Tensile Strength at Break 7.0 MPa MPa ISO 527-2 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ISO 1193 Melt Flow Index 7.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 7.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 65.0 °C °C ISO 11357-3 Softening Point max. 40.0 °C °C ASTM D1525 at 10N Softening Point max. 40.0 °C °C ISO 306 at 10N Softening Point max. 40.0 °C °C Vicat Softening Point Test at 10N Storage Temperature max. 86.0 °F °F - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) approx. 350.0 °C °C ASTM D1929 Decomposition Temperature (SDS) 360.0 °C °C Density (SDS) 940.0 kg/m³ kg/m³ typical value Melting Point (SDS) 65.0 °C °C Softening Point (SDS) 40.0 °C °C - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr