Enhanced TDS
Identification & Functionality
- Additives Included
- Blend
- Yes
- Chemical Family
- Function
- Resin
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM16131
- Single Ingredient
- No
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Processing Information
Profile Extrusion, Other Extrusion
- Typical melt temperature (Min / Recommended / Max) : 230°C / 250°C / 280°C.
- Drying time and temperature (only necessary for bags opened for more than two hours) : 4-8 hours at 80-90°C.
Properties
Technical Details & Test Data
- Technical Data
Viscosity-shear Rate
Shearstress-shear Rate
Dynamic Shear Modulus-temperature
Stress-strain
Secant Modulus-strain
Stress-strain (Isochronous) 104°F
Creep Modulus-time 104°F
Principal Information
- Group Principal Number
- S000003
- Principal
Other
- Color (SDS)
- Translucent
- Insoluble in (SDS)
- Water
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Thermal Properties
Value Units Test Method / Conditions Coefficient of Thermal Expansion 0.0001 /K /K ISO 11359-1 parallel, dry Coefficient of Thermal Expansion 0.0001 /K /K ISO 11359-2 parallel, dry - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr yr - Electrical Properties
Value Units Test Method / Conditions Dielectric Strength 24.0 kV/mm kV/mm IEC 60243-1 dry basis Volume Resistivity 10000000000.0 Ω-cm Ω-cm IEC 62631-3-1 dry basis - Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 11.0 kJ/m² kJ/m² ISO 179-1EA at -30°C, condensed, notched Hardness 64.0 Shore D Shore D at 15 sec Hardness 64.0 Shore A Shore A ISO 868 after 15s, dry Nominal Strain at Break min. 50.0 % % ISO 527-1 condensed, at break, nominal Nominal Strain at Break min. 50.0 % % ISO 527-2 condensed, at break, nominal Strain at Yield 4500.0 % % ISO 527-1 condensed Strain at Yield 4500.0 % % ISO 527-2 condensed Tensile Modulus 74000.0 psi psi ISO 527-1 condensed Tensile Modulus 74000.0 MPa MPa ISO 527-2 condensed Weld Load 5.0 kg kg ISO 1133 at 235°C - Physical Properties
Value Units Test Method / Conditions Density 1040.0 kg/m³ kg/m³ ISO 1183 condensed Density 1040.0 kg/m³ kg/m³ ISO 1183 dry basis Load/Unload Temperature 135.0 °C °C ISO 75-1 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 47.0 °C °C ISO 75-1 at 1.80 MPa, dry, deflection under load Load/Unload Temperature 135.0 °C °C ISO 75-2 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 47.0 °C °C ISO 75-2 at 1.80 MPa, dry, deflection under load Melt Volume-Flow Rate 2.0 cc/10min cc/10min ISO 1133 at 235°C Melting Point 182.0 °C °C ISO 11357-3 at 10°C/min Melting Point 182.0 °C °C ISO 11357-1 at 10°C/min Softening Point 146.0 °C °C ISO 306 at 50°C/h, 50N, dry Water Absorption 1.8 % % ISO 62 condensed - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 788.0-842.0 °F °F Bulk Density (SDS) 570.0-670.0 kg/m³ kg/m³ Decomposition Temperature (SDS) min. 662.0 °F °F Density (SDS) 1.04 g/cm³ g/cm³ Lower Explosion Limit (SDS) 94.0 % % at 85⁰C Melting Point (SDS) 360.0 °F °F