Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Country of Origin
- Function
- Resin
- Plastics & Elastomers Functions
- Product Code
- MITM12353
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Processing Information
Injection Molding
- Typical melt temperature (Min / Recommaneded / Max) : 250°C / 280°C / 300°C
- Typical mold temperature : 20 - 80 °C
- Dyring time and temperature (only for bags opened for more than two hours): 4 - 6 hours at 90°C
Properties
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000003
- Principal
Other
- Color (SDS)
- Clear colorless
- Insoluble in (SDS)
- Water
- Item Number
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains high molecular weight polymer(s). Effects due to processing releases: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Optical Properties
Value Units Test Method / Conditions Light Transmittance 92.0 % ISO 13468-1 Light Transmittance 92.0 % ISO 13468-2 - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 2.0 yr - Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 7.5 kJ/m² ISO 179-1EA at 23°C, dry, notched Charpy Impact Strength 7.0 kJ/m² ISO 179-1EA at -30°C, dry, notched Hardness 78.0 Shore D at 15 sec Hardness 78.0 Shore A ISO 868 at 15 sec Nominal Strain at Break min. 50.0 % ISO 527-1 condensed, at break, nominal Nominal Strain at Break min. 50.0 % ISO 527-2 condensed, at break, nominal Strain at Yield 61.0 % ISO 527-1 condensed Strain at Yield 61.0 % ISO 527-2 condensed Tensile Modulus 1670.0 MPa ISO 527-1 condensed Tensile Modulus 1670.0 MPa ISO 527-2 condensed - Physical Properties
Value Units Test Method / Conditions Density 1010.0 kg/m³ ISO 1183 condensed Density 1010.0 kg/m³ ISO 1183 dry basis Glass Transition Temperature (Tg) 150.0 °C ISO 11357-1 at 10°C/min, dry Glass Transition Temperature (Tg) 150.0 °C ISO 11357 at 10°C/min, dry Humidity Absorption 1.7 % ISO 62 at 23°C, dry Load/Unload Temperature 135.0 °C ISO 75-1 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 120.0 °C ISO 75-1 at 1.80 MPa, dry, deflection under load Load/Unload Temperature 135.0 °C ISO 75-2 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 120.0 °C ISO 75-2 at 1.80 MPa, dry, deflection under load Mold Shrinkage 0.8 % ISO 2577 normal, dry Mold Shrinkage 0.6 % ISO 2577 parallel, dry Mold Shrinkage 0.8 % ISO 294-4 normal, dry Mold Shrinkage 0.6 % ISO 294-4 parallel, dry Water Absorption 4.0 % ISO 62 at 23°C, dry - Material Composition
Value Units Test Method / Conditions Carbon Content 45.0 % ASTM D6866 - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 788.0-842.0 °F Bulk Density (SDS) 600.0 kg/m³ at 20°C Decomposition Temperature (SDS) min. 662.0 °F Lower Explosion Limit (SDS) 45.0 % at 85⁰C