Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Country of Origin
- Function
- Resin
- Plastics & Elastomers Functions
- Polymer Name
- Product Code
- MITM15802
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Processing Information
- Injection Molding
- Melt Spinning
Properties
- Physical Form
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000003
- Principal
Other
- Color (SDS)
- Colorless
- Insoluble in (SDS)
- Water
- Item Number
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness, (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Mechanical Properties
Value Units Test Method / Conditions Charpy Impact Strength 9.0 kJ/m² kJ/m² ISO 179-1EA at 23°C, condensed, notched Charpy Impact Strength 7.0 kJ/m² kJ/m² ISO 179-1EA at 23°C, dry, notched Charpy Impact Strength 9.0 kJ/m² kJ/m² ISO 179-1EA at -30°C, condensed, notched Charpy Impact Strength 8.0 kJ/m² kJ/m² ISO 179-1EA at -30°C, dry, notched Hardness 71.0 Shore D Shore D at 15 sec Hardness 71.0 Shore A Shore A ISO 868 at 15 sec Strain at Break min. 50.0 % % ISO 527-1 at break, condensed Strain at Break min. 50.0 % % ISO 527-1 Dry, at break Strain at Break min. 50.0 % % ISO 527-2 at break, condensed Strain at Break 5.0 % % ISO 527-2 condensed Strain at Break min. 50.0 % % ISO 527-2 Dry, at break Strain at Yield 5660.0 % % ISO 527-1 condensed Strain at Yield 5660.0 % % ISO 527-2 condensed Stress at Break 54.0 MPa MPa ISO 527-1 at break, condensed Stress at Break 54.0 MPa MPa ISO 527-1 Dry, at break Stress at Break 54.0 MPa MPa ISO 527-2 at break, condensed Stress at Break 54.0 MPa MPa ISO 527-2 Dry, at break Tensile Modulus 1220.0 MPa MPa ISO 527-1 condensed Tensile Modulus 1200.0 MPa MPa ISO 527-1 dry basis Tensile Modulus 1220.0 MPa MPa ISO 527-2 condensed Tensile Modulus 1200.0 MPa MPa ISO 527-2 dry basis - Physical Properties
Value Units Test Method / Conditions Density 1030.0 kg/m³ kg/m³ ISO 1183 dry basis Humidity Absorption 0.81 % % ISO 62 at 23°C, RH, 50% dry Load/Unload Temperature 129.0 °C °C ISO 75-1 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 42.0 °C °C ISO 75-1 at 1.80 MPa, dry, deflection under load Load/Unload Temperature 129.0 °C °C ISO 75-2 at 0.45 MPa, dry, deflection under load Load/Unload Temperature 42.0 °C °C ISO 75-2 at 1.80 MPa, dry, deflection under load Melting Point 189.0 °C °C ISO 11357-3 at 10°C/min Melting Point 189.0 °C °C ISO 11357-1 at 10°C/min Mold Shrinkage 1.1 % % ISO 2577 normal, dry Mold Shrinkage 1.1 % % ISO 2577 parallel, dry Mold Shrinkage 1.1 % % ISO 294-4 normal, dry Mold Shrinkage 1.1 % % ISO 294-4 parallel, dry Water Absorption 1.8 % % ISO 62 at 23°C, dry - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 662.0 °F °F Density (SDS) 1.03 g/cm³ g/cm³ Lower Explosion Limit (SDS) 98.0 % % at 85⁰C Melting Point (SDS) 372.0 °F °F Specific Gravity (SDS) 1.03 - Water = 1, liquid