ACEMATT® OK 607 LC is mainly used as a high-purity filler for e-coats due to its outstanding suspension behaviour and low electrical conductivity.
Properties
- Physical Form
- Soluble In
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S000006
- Principal
Storage & Handling
- Storage Conditions
- ACEMATT® OK 607 LC is inert and extremely stable chemically. However, due to their high specific surface area, they can absorb moisture and volatile organic compounds from the surrounding atmosphere. Therefore, we recommend storing the products in sealed containers in a dry, cool place, and removed from volatile organic substances.
- Even if a product is stored under these conditions, after a longer period it can still pick up ambient moisture over time, which could lead to its exceeding the specified moisture content.
- Recommended use-by date is 24 months after date of manufacture. Products more than 24 months old should be tested for moisture content before use in order to make certain that it is still suitable for the intended application.
Other
- Color (SDS)
- White
- Item Number
- Odor (SDS)
- Sweet
- Other Hazards
- Combustible material
- USA/DOT UN Number
- Not Applicable
- Chemical Properties
Value Units Test Method / Conditions Assay min. 98.0 % % ISO 3262-19 Ignited basis, silicon dioxide pH 6.3 - ISO 787-9 5% in Water - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 24.0 mo mo - Electrical Properties
Value Units Test Method / Conditions Electrical Conductivity max. 200.0 μS/cm μS/cm ISO 787-14 4% In Water - Physical Properties
Value Units Test Method / Conditions Moisture Content max. 6.0 % % ISO 787-2 at 105°C, 2 hours Oil Absorption 245.0 ml/100 g ml/100 g ISO 19246 DOA Particle Size 4.4 µm µm ISO 13320 D50 Particle Size 4.4 µm µm Laser Diffraction D(0.5) Specific Surface Area 130.0 m²/g m²/g ISO 9277 Nitrogen - Material Composition
Value Units Test Method / Conditions Carbon Content 5.5 % % ISO 3262-19 Sulfate Content max. 0.2 % % ISO 19350 - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 486.0 °F °F DIN 51794 Autoignition Temperature (SDS) 486.0 °F °F NFT 20 037 Boiling Point (SDS) 419.0 °F °F Decomposition Temperature (SDS) min. 230.0 °C °C Density (SDS) 2.0 g/cm³ g/cm³ DIN EN ISO 787-10 at 20°C Flash Point (SDS) 187.0 °F °F Closed Cup Flash Point (SDS) 187.0 °F °F DIN 51755 Ignition Temperature (SDS) 460.0 °C °C Log Partition Coefficient (Log Pow) (SDS) 3.67-4.64 - Oil/Water Melting Point (SDS) -130.0 °F °F Minimum Ignition Temperature (SDS) 460.0 °C °C Molecular Weight (SDS) 184.0 g/mol g/mol Solubility In Water (SDS) 96.0 g/L g/L at 25°C Specific Gravity (SDS) 0.885 - at 20°C, water = 1 Vapor Density (SDS) 7.67 kg/m³ kg/m³ At 20°C Vapor Pressure (SDS) 0.18 mm Hg mm Hg At 25°C Viscosity (SDS) 1.7 mPa.s mPa.s At 20°C pH (SDS) 6.0 - at 20°C, 50 g/l Suspension pH (SDS) 6.0 -