Enhanced TDS
Identification & Functionality
- Blend
- No
- CASE Ingredients Functions
- Chemical Family
- Chemical Name
- Plastics & Elastomers Functions
- Product Code
- MITM01656
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Labeling Claims
- Materials Features
Applications & Uses
- Coating End Applications
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Processing Information
LOTADER® 3210 can be extruded with standard polyolefin extrusion equipment with typical melt temperature of 270°C and up to 320°C-330°C. LDPE purge is recommended before extruder shutdown.
Properties
- Physical Form
- Soluble In
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTADER® 3210 is usually packed in waterproof bags or rigid containers with waterproof liner. It should be stored in dry conditions and be kept out of moisture in an aerated building.
- Improper storage conditions may cause degradation and could have consequences on physical properties of the product. It is recommended to reseal the bag or the liner after use to protect LOTADER® 3210 against moisture.
- Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- Colorless
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Slightly acrylic
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure).
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 600.0 % % ASTM D638 Elongation at Break 600.0 % % ISO 527 Flexural Modulus 120.0 MPa MPa ISO 178 Flexural Modulus 120.0 MPa MPa ISO 178 Hardness 46.0 HV HV ASTM D2240 Hardness 46.0 Shore D Shore D Shore Durometer Scale Hardness 46.0 HV HV ISO 868 Tensile Strength at Break 12.0 MPa MPa ASTM D638 Tensile Strength at Break 12.0 MPa MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ISO 1183 Density 0.94 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 5.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 5.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 107.0 °C °C ISO 11357-3 Softening Point 76.0 °C °C ASTM D1525 10N Softening Point 76.0 °C °C ISO 306 10N - Material Composition
Value Units Test Method / Conditions Butyl Acrylate Content 6.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) Maleic Anhydride Content 3.1 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 842.0 °F °F Bulk Density (SDS) 500.0 kg/m³ kg/m³ Decomposition Temperature (SDS) min. 572.0 °F °F Density (SDS) 940.0 kg/m³ kg/m³ at 68°F Melting Point (SDS) 203.0-225.0 °F °F