Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM01664
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Labeling Claims
- Materials Features
Applications & Uses
- Coating End Applications
- Compatible Substrates & Surfaces
- Plastics & Elastomers Processing Methods
- Processing Information
LOTADER® 4503 can be extruded with standard polyolefin extrusion equipment with typical melt temperature of 290°C and up to 320°C. LDPE purge is recommended before extruder shutdown.
Properties
- Physical Form
Packaging & Availability
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTADER® 4503 is usually packed in waterproof bags or rigid containers with waterproof liner. It should be stored in dry conditions and be kept out of moisture in an aerated building.
- Improper storage conditions may cause degradation and could have consequences on physical properties of the product. It is recommended to reseal the bag or the liner after use to protect LOTADER® 4503 against moisture.
- Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- White
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 750.0 % % ASTM D638 Elongation at Break 750.0 % % ISO 527 Flexural Modulus 20.0 MPa MPa ASTM D790 Flexural Modulus 20.0 MPa MPa ISO 178 Hardness 25.0 HV HV ASTM D2240 Hardness 25.0 Shore D Shore D Shore Durometer Scale Hardness 25.0 HV HV ISO 868 Tensile Strength at Break 9.0 MPa MPa ASTM D638 Tensile Strength at Break 9.0 MPa MPa ISO 527 - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ISO 1183 Density 0.94 g/cm³ g/cm³ ASTM D1505 Melt Flow Index 8.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 8.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 80.0 °C °C ISO 11357-3 Softening Point 45.0 °C °C ASTM D1525 10N Softening Point 45.0 °C °C ISO 306 10N - Material Composition
Value Units Test Method / Conditions Maleic Anhydride Content 0.3 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) Methyl Acrylate Content 20.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Decomposition Temperature (SDS) min. 350.0 °C °C Density (SDS) 0.95 g/cm³ g/cm³ at 68°F Melting Point (SDS) 85.0-95.0 °C °C Melting Point (SDS) 185.0-203.0 °F °F Differential Scanning Calorimetry Melting Point (SDS) 185.0-203.0 °F °F Differential Thermal Analysis