Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Plastics & Elastomers Functions
- Product Code
- MITM15436
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Labeling Claims
- Materials Features
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Compatible Substrates & Surfaces
- Plastics & Elastomers Processing Methods
- Processing Information
LOTADER® 4613T could be extruded with standard polyolefin equipment with typical melt temperature of 280°C and up to 310 - 320°C. LDPE purge is recommended before extruder shut-down.
Properties
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTADER® 4613T is usually packed in waterproof bags or rigid containers with waterproof liner. It should be stored in dry conditions and be kept out of moisture in an aerated building. Improper storage conditions may cause degradation and could have consequences on physical properties of the product. It is recommended to reseal the bag or the liner after use to protect LOTADER® 4613T against moisture.
- Shelf life is three years from the date of delivery, in unopened packaging.
Other
- Color (SDS)
- Colorless
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Slightly acrylic
- Other Hazards
- Contact with the product, when handled at high temperatures, can cause serious burns, At high temperature, products of thermal decomposition can be irritating to respiratory system Toxic effects cannot be excluded Possible irritation of respiratory system (by dust inhalation)., At high temperature, products of thermal decomposition can be irritating to skin Repeated or prolonged skin contact may cause allergic reactions with susceptible persons., At high temperature, products of thermal decomposition can be irritating to eyes Dust contact with the eyes can lead to mechanical irritation., Inert polymer not biodegradable on the basis of its structure, Thermal decomposition giving toxic products Decomposition products: See chapter 10
- Protect from Freezing
- No
- Temperature Control
- No
- USA/DOT UN Number
- Not Applicable
- Material Composition
Value Units Test Method / Conditions Maleic Anhydride Content 0.3 - Fourier Transform Infrared Spectroscopy (FTIR) Methyl Acrylate Content 24.5 - Fourier Transform Infrared Spectroscopy (FTIR) - Mechanical Properties
Value Units Test Method / Conditions Flexural Modulus 23.0 MPa MPa ASTM D790 Flexural Modulus 23.0 MPa MPa ISO 178 Hardness 81.0 HV HV ASTM D2240 Hardness 81.0 - Shore Durometer Scale Hardness 81.0 HV HV ISO 868 - Physical Properties
Value Units Test Method / Conditions Density 0.95 g/cm³ g/cm³ ASTM D1525 Melt Flow Index 7.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 7.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 98.0 °C °C ISO 11357-3 Softening Point 41.0 °C °C ASTM D1525 on compression molded samples Softening Point 41.0 °C °C ISO 306 on compression molded samples - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 450.0 °C °C Decomposition Temperature (SDS) min. 300.0 °C °C Density (SDS) 900.0-950.0 - at 20°C Melting Point (SDS) 70.0-102.0 °C °C DIN 51007 Melting Point (SDS) 70.0-102.0 °C °C Differential Scanning Calorimetry Melting Point (SDS) 70.0-102.0 °C °C Closed Cup Melting Point (SDS) 70.0-102.0 °C °C Differential Thermal Analysis - Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 -