Features & Benefits
- Labeling Claims
- Materials Features
- Product Highlights
- Due to the high butyl acrylate content, LOTRYL® 35BA40T can be used for applications where flexibility and polarity are required.
- Thanks to its high fluidity, LOTRYL® 35BA40T is suitable for the formulation of hot melt adhesives.
- It can also be used in polyesters as an impact modifier for high fluidity compounds.
Applications & Uses
- Adhesive & Sealant End Applications
- Coating End Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
- Contains any chemicals listed on Prop 65 (including impurities, residues, catalysts, monomers, and by-products and excluding heavy metals)?
Technical Details & Test Data
- Processing Details
LOTRYL® 35BA40T can be processed with standard polyolefin extrusion equipment up to 300°C and it is recommended to purge the equipment after a run is completed. If LOTRYL® 35BA40T is used pure for instance with blown or cast film technology, standard temperature settings could be:
Zone 1 Zone 2 Zone 3 Zone 4 Fittings-Channels Die 150 - 170°C 170°C 170°C 170°C 170°C 170°C Final profile and settings depend on the line and multilayer structure being run.
Packaging & Availability
- Packaging Type
Principal Information
- Group Principal Number
- S002377
- Principal
Storage & Handling
- Storage and Shelf Life Conditions
- LOTRYL® 35BA40T should be stored in standard conditions and protected from UV-light. Improper storage conditions may cause degradation and could have consequences on physical properties of the product. Due to its physical properties, it may be possible that the LOTRYL® 35BA40T shows some caking. This is particularly true during summer time.
- Three years from the date of delivery, in unopened packaging. For any use above this limit, please refer to our technical services.
Other
- Color (SDS)
- Translucent
- Insoluble in (SDS)
- Water
- Item Number
- Odor (SDS)
- Ester like
- Other Hazards
- Processing may release vapors and/or fumes which cause eye, skin and respiratory tract irritation, The product, in the form supplied, is not anticipated to produce significant adverse human health effects. Contains polymer(s). Effects due to processing releases or residual monomer: Irritating to eyes, respiratory system and skin, Prolonged or repeated exposure may cause: headache, drowsiness, nausea, weakness. (severity of effects depends on extent of exposure), Handle in accordance with good industrial hygiene and safety practice. (pellets/granules) This product may release fume and/or vapor of variable composition depending on processing time and temperature.
- USA/DOT UN Number
- Not Applicable
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 3.0 yr yr - Mechanical Properties
Value Units Test Method / Conditions Elongation at Break 400.0 % % ASTM D638 Elongation at Break 400.0 % % ISO 527-2 Flexural Modulus max. 10.0 MPa MPa ASTM D790 Flexural Modulus max. 10.0 MPa MPa ISO 178 Hardness 60.0 Shore A Shore A Hardness 60.0 Shore A Shore A ASTM D2240 Hardness 60.0 Shore A Shore A ISO 868 Tensile Strength at Break 1.8 MPa MPa ASTM D638 Tensile Strength at Break 1.8 MPa MPa ISO 527-2 Tensile Strength at Break 1.8 MPa MPa ISO 527 compression molded - Physical Properties
Value Units Test Method / Conditions Density 0.94 g/cm³ g/cm³ ASTM D150 Density 0.94 g/cm³ g/cm³ ISO 1193 Melt Flow Index 40.0 g/10min g/10min ASTM D1238 at 190°C, 2.16kg Melt Flow Index 40.0 g/10min g/10min ISO 1133 at 190°C, 2.16kg Melting Point 89.0 °C °C ISO 11357-3 Softening Point 134.0 °C °C Ring and Ball Test Softening Point max. 40.0 °C °C ASTM D1525 at 10N Softening Point 134.0 °C °C ASTM E28 Softening Point max. 40.0 °C °C ISO 306 at 10N Softening Point max. 40.0 °C °C Vicat Softening Point Test at 10N - Material Composition
Value Units Test Method / Conditions Butyl Acrylate Content 35.0 %(W/W) %(W/W) Fourier Transform Infrared Spectroscopy (FTIR) - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 662.0 °F °F Bulk Density (SDS) 500.0 kg/m³ kg/m³ Decomposition Temperature (SDS) min. 662.0 °F °F Density (SDS) 0.92-0.98 g/cm³ g/cm³ at 68°F Melting Point (SDS) 140.0-212.0 °F °F