Enhanced TDS
Identification & Functionality
- Blend
- No
- CASE Ingredients Functions
- Chemical Family
- Product Code
- MITM04040
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Labeling Claims
Applications & Uses
- Coating End Applications
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Ink & Toner End Applications
- Markets
- Applications
Properties
- Physical Form
- Note
Drying the coatings at 300°F for 30 minutes simulates final propertes of the resin.
- The white lacquers were formulated at a titanium dioxide/binder ratio (solids basis) of 30/70. The properties were determined after coatings were sprayed on Bonderite 1000 solution.
- The degree of flaking at the scribed cross hatch is rated on a 0 (no failure) to 5 (complete lift off) scale.
- The degree of cracking at the bend over each mandrel is rated on a 0 (no failure) to 10 (complete flaking) scale.
Regulatory & Compliance
Technical Details & Test Data
- Properties in White Lacquers
Tukon Hardness Whiteness (K Color Low Numbers Best)
Cross Hatch³ 30 min. at 180°F 13.2 30 min. at 300°F 8.1 30 min. at 180°F 4 30 min. at 300°F 20.4 16 hrs. at 350°F 11.7 30 min. at 300°F 3 Pencil Hardness Flexibility, "1/8,1/4, 1/2 Mandrels⁴ Mustard Staining (30 min. Exposure) 30 min. at 180°F F 30 min. at 180°F 6,5,4 30 min. at 180°F None 30 min. at 300°F 3H 30 min. at 300°F 5,4,3 30 min. at 300°F None Gloss, 20° Printing, 2 psi for 1 hr. at 140°F Gasoline Resistance (15 min. Exposure)
30 min. at 180°F 82 30 min. at 180°F Light 30 min. at 180°F Slightly Soft 30 min. at 300°F 80 30 min. at 300°F None 30 min. at 300°F Dull Gloss, 60° Knife Adhesion Spray Conditions 30 min. at 180°F 94 30 min. at 180°F Very Poor Viscosity, #4 Ford Cup, sec. 15 30 min. at 300°F 92 30 min. at 300°F Poor Solids Content, % 37
Packaging & Availability
Principal Information
- Group Principal Number
- S000005
- Principal
Storage & Handling
- Storage Conditions
- Keep combustible and/or flammable products and their vapors away from heat, sparks, flames and other sources of ignition including static discharge.
- Processing or operating at temperatures near or above product flashpoint may pose a fire hazard.
- Use appropriate grounding and bonding techniques to manage static discharge hazards.
- Failure to maintain proper volume level when using immersion heaters can expose tank and solution to excessive heat resulting in a possible combustion hazard, particularly when plastic tanks are used.
- Store products in tightly closed original containers at temperatures recommended on the product label.
Other
- Color (SDS)
- Pale yellow
- Flammable Nature (SDS)
- May form combustible dust concentrations in air during processing, handling or other means
- Item Number
- Odor (SDS)
- Acrylic odor
- Other Hazards
- If converted to small particles during further handling, processing, or by other means, may form combustible dust concentrations in air, Dust contact with the eyes can lead to mechanical irritation, Contact with dust can cause mechanical irritation or drying of the skin.
- USA/DOT UN Number
- Not Applicable
- Mechanical Properties
Value Units Test Method / Conditions Hardness 14.0-15.0 HV of clear films Ultimate Hardness 14.0-15.0 KHN - Physical Properties
Value Units Test Method / Conditions Bulk Density 9.6 lb/gal At 25°C Glass Transition Temperature (Tg) 82.0 °C - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) 393.0 °C Liquid Density (SDS) 0.64 g/cm³ Volatile Content (SDS) max. 2.0 %