Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Code
- MITM04867
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Key Features and Benefits
- Product Features:
- Satiny finish
- Low coefficient of friction
- Remains flexible over a wide range of temperatures
- Good release properties with a low coefficient of friction
- Consistent and uniform dip spin or spray application performance
- Resistant to a variety of oil and solvents
- Product Benefits:
- Attractive component appearance to secure customer satisfaction
- Ability to meet lubrication requirements for the component
- Application for a variety of environmental performance requirements
- Ability to meet lubrication and assembly requirements for the component and application
- Versatile application techniques to minimize operation costs
- Ability to design into a variety of component applications with differing environmental exposure needs
- Product Features:
Applications & Uses
- Application Area
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Cure Method
- Markets
- Applications
- Application and Usage Information
- Product Application
- Fasteners
- Sliding Rails
- Lock mechanisms
- Seat belt components
- Latches
- Mechanisms
- Usage Information
- Surface Preparation
- For maximum resistance to wear, corrosion and abrasion, the following procedures are recommended:
- Steel: Degrease, grit blast, and/or chemically pretreat with Bonderite M-ZN 20 (know as Granodine 20),
- Bonderite M-MN 2 (known as Lubrite 2), or equivalent
- Stainless Steel: Degrease grit blast.
- Aluminum: Degrease, pretreat with Bonderite M-CR 1200S (known as Alodine 1200S) or equivalent, anodize.
- Mixing
- BONDERITE® S-FN 330 ACHESON can be spray applied undiluted. However, to obtain maximum smoothness, dilute the product with Methyl Ethyl Ketone (MEK) or BONDERITE L-FG SB-2 ACHESON (known as Henkel solvent SB-2) in the ratio of three parts product (by weight) to one part solvent. If parts are to be dipped, a 3:2 (product:solvent) weight ratio is recommended. If dip-spin equipment is used, adjust the product to 20- 30 seconds on a #2 Zahn cup (neat product may already be in this range).
- Application
- Use an external-atomizing spray gun with 35 to 50 psi air pressure and adjust the gun to give a well-atomized spray. For optimum performance, the final coating thickness should be 0.0003-0.0010 inches (0.008 to 0.025 millimeters). When properly applied, the coating will be even and free of runs, blisters, or "fish eyes." Some electrostatic spray systems may be used to apply BONDERITE® S-FN 330 ACHESON. Contact our Specialty Coatings Business Group's Technical Service Department for details.
- BONDERITE® S-FN 330 ACHESON can also be applied by dipping. The product should be diluted 3:2 (product: solvent) by weight with MEK. The average dip coating will produce a heavier coat, but a pre- cure of ten minutes at 121° to 135°C (250° to 275°F) or one minute at 177°C (350°F) is required between dips. Dip- spin will require two or three coats. A partial cure of one minute at 177°C (350°F) is required between coats.
- Curing
- BONDERITE® S-FN 330 ACHESON must be air-dried to the touch (2-5 minutes) before being placed in the curing oven. For optimum corrosion and wear resistance, cure the coating for one hour at 160°C (325°F) in an air-circulating oven or under infrared lamps. Acceptable cure cycles include one hour at 150°C (300°F), 10 minutes at 175°C (350°F), 8 minutes at 204°C (400°F), or 5 minutes at 260°C (500°F). Note that as cure temperature increases, cure time becomes more critical. Degree of cure may be monitored by the color of the oating. As the cure progresses, the coating will gradually change in color from light blue to dark green. Cured coatings can only be removed by sandblasting or applying strong caustic solutions.
- Surface Preparation
- Product Application
Properties
- Physical Form
Packaging & Availability
Storage & Handling
- Storage and Shelf Life Information
- Keep container tightly closed when not in use. Store in a cool, well ventilated area. Keep away from heat, sparks, and open flame. Protect material from direct sunlight. Ground and bond containers when transferring materials. Empty containers may retain hazardous properties. Follow all MSDS/label warnings even after container is emptied. Shelf life for this product is 2 years from date of qualification under original seal.
Other
- Application Temperature
- 130.0 °C
- Autoignition Temperature (SDS)
- min. 272.0 °C
- Boiling Point (SDS)
- 78.0 °C
- Coefficient of Friction
- 0.05-0.07
- Color
- Green
- Color (SDS)
- Blue
- Coverage
- 6.81 m²/kg
- Density
- 0.96 kg/L
- Flash Point
- 10.0 °C
- Flash Point (SDS)
- 10.0 °C
- Group Principal Number
- S000218
- IATA/ICAO Proper Shipping Name
- Coating Solution
- IATA/ICAO UN Number
- UN 1139
- IMO/IMDG Proper Shipping Name
- Coating Solution
- IMO/IMDG UN Number
- UN 1139
- Item Number
- Lower Explosive Limit (SDS)
- 1.1 %
- Melting Point (SDS)
- max. 0.0 °C
- Odor (SDS)
- Pungent, alcohol
- Principal
- Shelf Life
- 24.0 mo
- Solid Content
- 25.0 %
- Specific Gravity (SDS)
- 0.97-0.99
- Storage Temperature
- 41.0-86.0 °F
- USA/DOT Proper Shipping Name
- Coating Solution
- USA/DOT UN Number
- UN1139
- Upper Explosion Limit (SDS)
- 36.5 %
- Viscosity
- 60.0-150.0 mPa.s
- Viscosity (SDS)
- 60.0-150.0 cPs
- Volatile Organic Compounds (VOC)
- 715.0 g/L
- Shelf Life & Stability
Value Units Test Method / Conditions Shelf Life 24.0 mo mo - Mechanical Properties
Value Units Test Method / Conditions Coefficient of Friction 0.05-0.07 - as static - Physical Properties
Value Units Test Method / Conditions Coverage 6.81 m²/kg m²/kg of wet product, at 25μm dry film thickness Density 0.96 kg/L kg/L Flash Point 10.0 °C °C Storage Temperature 41.0-86.0 °F °F Viscosity 60.0-150.0 mPa.s mPa.s of wet product - Material Composition
Value Units Test Method / Conditions Solid Content 25.0 % % by weight of wet product Volatile Organic Compounds (VOC) 715.0 g/L g/L of wet product - Application Information
Value Units Test Method / Conditions Application Temperature 130.0 °C °C continuous - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Autoignition Temperature (SDS) min. 272.0 °C °C Boiling Point (SDS) 78.0 °C °C Flash Point (SDS) 10.0 °C °C Closed Cup Lower Explosive Limit (SDS) 1.1 % % Melting Point (SDS) max. 0.0 °C °C Specific Gravity (SDS) 0.97-0.99 - Upper Explosion Limit (SDS) 36.5 % % Viscosity (SDS) 60.0-150.0 cPs cPs